Electronics Forum | Thu Mar 17 03:07:17 EST 2005 | Chua
Hi, We are running lead free at wave solder now and the spray flux system is down. If we are going to able the flux manually, what problem will we be facing with the excess flux able. Appreciate for the advise.
Electronics Forum | Thu Mar 17 22:14:42 EST 2005 | Chua
Hi Davef, Thanks for your advise...... We are running no-clean process. If there is white residues after few days.....is it cause by those excess flux. Thanks
Electronics Forum | Thu Mar 17 10:14:30 EST 2005 | davef
If you're washing the boards properly, you should see any problems, maybe a little extra floaming, but that won't be too bad. If you're running no clean, you need to aplly flux according to your supplier's recommendations. If you decide not to foll
Electronics Forum | Fri Jul 23 14:41:41 EDT 2004 | Steve Stach
Dear JSK, It sounds like the root causes of your problem are two fold. First, excessive heat will polymerize the abietic acid found in rosin forming neo-abietic diamers and polymers which are much less soluble than the parent monomer. There are
Electronics Forum | Thu Mar 17 22:47:29 EST 2005 | davef
That would be our first guess, also. Get the stuff analyzed to be sure. Another clue is if the white stuff disappears when you hit it with hot air from a rework station. The hot air is activate the flux. Good troubleshooting tool, but you're subj
Electronics Forum | Mon Sep 24 11:12:56 EDT 2001 | nwyatt
Hi. We are currently using an unconventional method to rework a micro BGA - removing component with hot air, fluxing the area, placing the part with pick and place, then reflowing it in the oven. The reason we are doing it this way and not with a r
Electronics Forum | Fri Mar 21 21:13:03 EST 2003 | iman
Russ, u mean excess flux causes "blow hole" defect?
Electronics Forum | Tue Sep 25 09:57:40 EDT 2001 | nwyatt
In regards to your last question, - problem is failures and most think it is due to too much flux - we apply flux with a brush - amount applied depends on the operator applying it - the flux is very thick and will hold the part in place before reflo
Electronics Forum | Fri Apr 04 14:49:51 EDT 2008 | tombstone
Flux seperation is a common problem observed due to expiration of paste. The symptom is a yellow layer of flux when you open the jar. Excess flux separation will cause priting problems such as smearing and slumping.
Electronics Forum | Mon Sep 24 20:38:27 EDT 2001 | davef
Mike's comments are well taken. Your technique works fine with BGA, but uBGA are less forgiving. Again, let's take about: * Specifics of the problem. * Amount and method of applying flux. * What's holding the uBGA in-place before the solder ball an