Electronics Forum | Wed Feb 20 23:17:34 EST 2002 | surachai
I AM JUST EVALUATION LEAD FREE EVALUATION AND FOUND THE BIG PROBLEM OF SOLDER CRACK BETWEEN TERMINAL OF COMPONENT AND THE INTERMETALLIC LAYER OF LEAD FREE ALLOY BUT DON'T FIND ANY CRACK BETWEEN SOLDER AND SURFACE OF PCB , COULD YOU HELP ME VERIFY T
Electronics Forum | Wed Oct 07 15:44:43 EDT 1998 | CW
There's a good article on lead-free assembly of mixed technology in the May issue of SMT Magazine (pg. 52)
Electronics Forum | Fri Dec 13 16:39:42 EST 2002 | Gris
Hi, Look for papers on SMTA there are a lot of papers on lead free rework. If you dont find any let us know here I am sure you will receive many. Here are a just a few http://www.google.com/search?hl=en&ie=UTF-8&oe=UTF-8&q=%22lead+free+rework%22&
Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Tue Oct 18 19:34:02 EDT 2011 | warwolf
so there is no one here baised in New Zealand that wants to buy our SAC305 solder dross and recycle it, we have about 120KG at the moment, anyone intrested?
Electronics Forum | Wed Oct 19 20:04:06 EDT 2011 | warwolf
yeah I’ve tried to go down the road of internal recycling but the company carnt justify spending 20k on a machine that does it. Ah but where still onto it in other places though our SMT department has very minimal wastage on solder paste as we have b
Electronics Forum | Wed Oct 19 11:33:15 EDT 2011 | caerleon
easier if you recycled on-site? You can still send off for reclaimation the oxide powder that your left at the end of the process. Failing that talk to your supplier to see if they have arrangements to do this for you or look at reducing dross - i f
Electronics Forum | Fri Oct 28 21:46:35 EDT 2011 | rdh_41
Hi , I'm interested in Tin and hoping to open long-term business relationship with your company. We are Taiwan-based company dedicate in Tin (Sn). We are looking for opportunity to work with you. And it would be great if you have large quantity of t
Electronics Forum | Sun Sep 17 02:48:41 EDT 2006 | Eric
Anyone know any international standard (e.g. IPC, JIS) for the SAC lead free solder strength ? If no, any industrial / company standard for it ? Besides, any mathematical model which can help to calculate it.... express in "Force / area "
Electronics Forum | Fri Mar 14 05:38:42 EDT 2008 | meritajs
Hello Could somebody inform us about real consumption of lead free solder alloy SN100C on your wave solder process. We do not use some antiaxidant and had had alloy consumption about 1 kg per hour. What is your experiance? All sugestion will be well