Electronics Forum | Fri Sep 19 15:52:18 EDT 2008 | davef
This is not something that we'd expect to see on NiPdAu finished leads. Help us understand the extent of the problem better. From your picture, it looks like a band of copper color with black on the outer portions of the copper color that bleeds int
Electronics Forum | Mon Oct 19 15:43:37 EDT 2009 | dilogic
We have a problem with QFN IC's with NiPdAu plated pads. Our ULC's don't see the pads due to the almost ideal reflection. Vision sees the pads almost black. As we don't have OAL-cameras (which can help in this case, I assume), I am thinking of back-l
Electronics Forum | Mon Sep 20 11:21:48 EDT 2010 | tony1
I have this NiPdAu small QFN packge sizes less than 2x2. I tried to do solderability Dip And Look test and there's always some units no wet on either ground pad and small I/O. Can someone help to explain why is this so difficult to set on this surfac
Electronics Forum | Tue Apr 26 03:28:26 EDT 2005 | Just mee
What test is applicable to check for QFN package with NiPdAu leadframe if leads/pad are solderable? what are the options other than dip and look solderability testing? Thanks,
Electronics Forum | Fri Oct 20 05:55:16 EDT 2006 | Eric Chen
40% in wetting problem. I would like to know any specific reflow profile in order to acheive good wetting at this type of lead. Besides, any specific paste e.g. halide containing paste required
Electronics Forum | Mon Feb 19 15:32:42 EST 2007 | blnorman
We use SnPb paste and bar with leaded and non-leaded component finishes. The predominant finish on components we use is Tin, there are a few NiPdAu. We've had no problems with the component finishes used in the SnPb process.
Electronics Forum | Fri Sep 19 15:23:33 EDT 2008 | vladig
All I can say is my regular "Get it analyzed", so you'll know what the streak is. Regards, Vladimir
Electronics Forum | Sat Sep 20 09:31:42 EDT 2008 | vladig
Wise move :-) Please let me know the results of the analysis and we can take it from there. Vlad
Electronics Forum | Wed Sep 22 15:33:54 EDT 2010 | davef
Comments are: * First, no one is looking at your posting. You need to post in the 'SMTnet Production Forum' [top of the page]. This 'SMTnet Site Support Forum' is for whiners that want to complain to Neil about problems in logging-in, font that's to
Electronics Forum | Wed Mar 14 10:42:20 EDT 2018 | jon_roberts
Dave, thanks. I was going to change Cu/PD/Au to Ni/Pd/Au and then my question is: Has anyone had soldering issue with components (ICs) with the above finish during reflow and/or had to change the oven profile to improve the wetting. Sorry for confusi