Electronics Forum | Tue May 13 06:57:10 EDT 2003 | davef
Your vendor site is totally correct. 2Ag is an excellent solder, but it does nothing to prevent tin and gold from reacting chemically. An earlier poster is correct gold goes into solution in liquid solder very fast, less than a second. Gold and ti
Electronics Forum | Fri Aug 26 09:57:21 EDT 2005 | russ
The Immersion gold is not a problem with BGAs specifically but "black pad" which can be present anywhere. The unfortunate thing with BGAs is you cannot see it. Personally I hate white tin. It is okay for single sided boards running no-clean, but c
Electronics Forum | Wed Aug 06 16:35:31 EDT 2003 | Carol
This is an old topic, but keeps coming up. Solderability and reliability issues with SMT gold plated terminations when used with tin/lead solder paste/hassle finish PWB. I need to know which standard (mil, IPC, J-STD??) tells you all about the probl
Electronics Forum | Wed Aug 06 20:50:42 EDT 2003 | davef
Well, if it "keeps coming up", let's take a pass at keeping down. For: * Requirement that gold be removed from components, pads, etc. is J-STD-001C, 5.4.1 * Context of that requirement [J-STD-001C, 5.4.1] and 6 or 7 references are in IPC-HDBK-001.
Electronics Forum | Fri May 03 16:06:44 EDT 2013 | hegemon
To be short, no change in profile is going to get you through this. As I recall the point of hard gold is to retard the wetting process, so no surprise here. For example a connector might have hard gold plating at the mating surface, but not at t
Electronics Forum | Fri Aug 26 14:15:16 EDT 2005 | David
Where could I find more information regarding the double sided reflow and flux problems with white tin?
Electronics Forum | Fri Aug 26 09:48:11 EDT 2005 | David
I have heard that there are problems using immersion gold on PCBs when working with BGAs. Is this correct? Is white tin more suitable?
Electronics Forum | Tue Jun 13 08:17:06 EDT 2006 | davef
The solder alloy does not change based on the flux. Your potential for embrittlement is the same [providing the metal of the solders are the same] with either solder. We would guess the OA flux is [and drag tinning are] removing corrosion from the
Electronics Forum | Mon May 20 15:43:01 EDT 2013 | ngotranbestek
Hi I meet problem by PCB with diameter 300cm and thick 6mm i used tin-lead with profile normal, soak time 60-90 sec, Temp peak is 220 degree C, But solder see not good, not shiny. Any body recomend help me to fix this problem for Hard gold playing.
Electronics Forum | Mon Jun 12 07:42:56 EDT 2006 | brian.perry@suntroncorp.com
We are placing a gold plated device (LCC) to a NiAu PCB using a SnPb No-clean solder. We're noticing quite a bit of difficulty with reliable joints (intermittent connectivity) and if we have to rework a particular device, adjacent devices of this sa