Electronics Forum | Tue May 23 09:01:21 EDT 2000 | Wirat S.
Dear all friend, I found problem of soldering bridging between SMT Chip terminal & Glue , but under the chip body. My process was double side SMT assembly with bottom side adhesive & heat curing, then wave soldering with water soluble flux (OS type)
Electronics Forum | Thu Jun 24 11:41:10 EDT 1999 | John Thorup
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel
Electronics Forum | Sun Apr 05 18:36:41 EDT 1998 | Graham Naisbitt
Sylvia, I believe you will find that contrary to Scott Cooks submission, that the work carried out by Robert Clark of Hughes Missile Systems at (then) Tuscon Arizona formed the basis of the MIL-F-14256 spec which "Qualified?" or at least "Approved" O
Electronics Forum | Wed Sep 15 23:15:55 EDT 2004 | pdeuel
Im with Pete, Zero defects. We have high defect rate for many reasons. No line tech, operators set up and run then when QA reports defects engneers are called. Not to make people mad but our process engneers are lacking practical experance to fix pro
Electronics Forum | Wed Sep 16 08:46:50 EDT 1998 | Chrys
Hi Folks, Need to draw upon the vast expertise in this forum... Whenever you fill a new wave solder machine with fresh bar solder, it seems to produce more than the normal amount of dross for a few weeks. I always understood this to be the solder "c
Electronics Forum | Tue Sep 22 13:14:27 EDT 1998 | Chrys
| We are getting into a lot of double sided boards offlate. Our customer is loading a lot of RNETS, Diodes ( MINLS, SOT23s and other 2 leaded diodes ). We are processing it through a traditional glue process and wave soldering the SMT parts along wit
Electronics Forum | Mon Sep 20 14:46:03 EDT 1999 | Dave F
| Hi all, | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are TH, the S
Electronics Forum | Mon Sep 20 17:20:08 EDT 1999 | Earl Moon
| | Hi all, | | | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are
Electronics Forum | Mon Sep 20 17:36:46 EDT 1999 | Dave F
| | | Hi all, | | | | | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | | | | | We are producing VGA cards and mother boards for PC's all components to be wave so
Electronics Forum | Tue Sep 21 07:47:31 EDT 1999 | Wolfgang Busko
| | Hi all, | | | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are