Electronics Forum | Fri Sep 15 05:48:24 EDT 2000 | carsonho
Have any experience that Sn/Pb plated integrated circuit products will appear some rainbowbridge-like substance after exposing at conditions of 121degC, 100%RH and 15psi for 48hours or above? The rainbow bridge substance was analyzed by EDAX and fou
Electronics Forum | Fri Sep 15 05:48:11 EDT 2000 | carsonho
Have any experience that Sn/Pb plated integrated circuit products will appear some rainbowbridge-like substance after exposing at conditions of 121degC, 100%RH and 15psi for 48hours or above? The rainbow bridge substance was analyzed by EDAX and fou
Electronics Forum | Tue Aug 22 11:03:45 EDT 2000 | Dr. Ning-Cheng Lee
Hi Kelvin, Regarding to the surface finish of the leads, Sn or Pd may be the direction that the industry takes. First of all, the answer must be "Pb-Free", limiting our choices. Sn has good solderability, and it won't have too great of an impact o
Electronics Forum | Thu Jul 20 17:07:49 EDT 2000 | JACKIE O'ROARK
Hello Bob, I am going to be working with a 5 Mil Flex circuit. There are 2 components to be placed on. I thought of using the conductive glue but after reading your message not recomending it, I am swayed againist it. What is the best way to place
Electronics Forum | Thu Jun 22 17:17:27 EDT 2000 | Bill Schreiber
The U.S. Environmental Protection Agency (EPA) has finally taken a progressive position by creating the Environmental Technology Verification (ETV) Program to verifiy the environmental safety, user safety and efficacy of products prior to their purch
Electronics Forum | Thu Jun 08 10:52:37 EDT 2000 | rolandos1
Hello, My name is Rolando and I want to know more about gold fingers protectors. Our current problem is on SMT line which is used with one board with gold pads and while normal production we get solder paste contaminations on these pads, recently o
Electronics Forum | Tue May 08 08:41:29 EDT 2001 | caldon
Hmmmmm........I am thinking!!!!! Cleaning is the final process in our situation. After cleaning we have no need for the fiducials. Is the haze causing fiducial recognition problems? Ideally what you are looking for is a contrast between fiducial and
Electronics Forum | Mon May 28 04:29:16 EDT 2001 | hello
we met the same problem with audit, and i make a tooling log for each stencil and in tooling log , set up some criteria for checking such as tension , mechanical damage, printing result ect. The stencil will be checked periodicly by process engineer,
Electronics Forum | Mon May 21 12:23:08 EDT 2001 | davis_brinkley
Why would you want AutoProgram for DOS? AutoProgram ver 5.3.2 is avilable from Quad Systems and is supported for using Windows 3.1.1 This is the latest rev for AutoProgram it is not supported for other operating systems because there is no more resea
Electronics Forum | Wed Jun 06 13:38:15 EDT 2001 | Michael Parker
To expand on Wolfgangs reply, I suggest you contact your local SRT rep. We recently had the same type of problem as yourself. This is the path we followed. Arrange for operator training, for yourself first, then the operators after you get the machi