Electronics Forum | Thu Jul 15 09:27:12 EDT 1999 | Erick Russell
Earl, Srt makes a system called the summit 2100D. Its a relatively new product but it is designed for rework applications. The programming is simple and interfaces well with other srt products. As with any dispensing system, you have to clean th
Electronics Forum | Mon Jun 21 22:27:57 EDT 1999 | John K.
We're a CM doing low volume/high mix and are considering buying from one of the two big names, TR** or Sp*******/El*********. We need saponified wash for some of our no-clean over wave; the great majority is OA from our SMT lines. Any thoughts?
Electronics Forum | Fri Jun 18 16:36:29 EDT 1999 | John Thorup
| Has there anyone bold enough to try this in their shops? My cubemate just got through telling me that at his last shop, they had bare copper boards (no HASL, no OSP, no nothing), with minimal solderability problems. I'd hate to have to clean what
Electronics Forum | Tue May 25 10:49:34 EDT 1999 | Deon Nungaray
.025" you should wipe under stencil surface after every 2 or 3 print cycles with a lint free cloth or lint free tissue. When performing this operation you can also lightly soak cloth or wipe in alcohol. Regards, Deon Nungaray SMT MFG Process Engin
Electronics Forum | Thu May 06 09:24:06 EDT 1999 | Joe Manzur
Kevin, We are also looking at printing adhesive. Our application involves printing glue on the underside of the board, once it has gone through the dip, axial & radial process. In otherwords, there are leads cut and clinched and we have to mill out
Electronics Forum | Wed Apr 21 03:10:37 EDT 1999 | Richard Cooper
To all who will be potentially my salvation, I am currently researching Polyimide stencils for possible use and manufacture. If I may be indulged - with due reference to all past enquiries and notes on the subject - can anyone offer an up to date op
Electronics Forum | Tue Apr 06 17:27:24 EDT 1999 | Kennyv
I am getting ready to purchase a spray fluxing system for a no-clean process. I have narrowed it down to the Nordson or Dover system. Does anyone have any experience with either. If so can you relate with me. I am a little leary of the Nordson be
Electronics Forum | Wed Mar 24 23:04:00 EST 1999 | Al O Owzitgon
| We are dealing with down time accredited to the Pumps getting clogged with dried glue. We have decided to purge all spindles at 6 hour intervals. We are looking at making this process automated. Has anybody tried this and if so, is there a way to s
Electronics Forum | Wed Feb 24 01:08:10 EST 1999 | Joe Cameron
Has anyone used the mechanical stencil foil tensioning system from certain company that eliminates using stencil frames and epoxy & mesh? Any comments on whether it's worth looking into? We go through product revisions like we go through clean sock
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be