Electronics Forum | Mon Oct 21 11:03:15 EDT 2013 | davef
I don't know about the papers that you seek. Try: Rakesh Kumar, Specialty Coating Systems, Inc., 7645 Woodland Drive, Indianapolis, IN 46278; 317-472-1266 F317-244-1215 rkumar@scscoatings.com
Electronics Forum | Mon Apr 02 01:24:52 EDT 2007 | Haris
Dear all, I want to know the difference between the CSP and the BGA (I think there is only in the mesh pin difference). Secondly, if their solder balls have same dia, LxBxH are also same with the the manufacturing of the pin coating chemical elemen
Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Thu Nov 21 11:19:58 EST 2013 | davef
Generally, solder connections and leads are conformal coated, unless there is a reason not to coat them.
Electronics Forum | Tue May 23 15:40:17 EDT 2000 | larry
We currently use both Humiseal and Conap with OA flux. The flux MUST me cleaned off the assembly before coating. I know that Humiseal has coatings that are compatiable with no cleans as long as your processes are defined properly before your coating
Electronics Forum | Fri Jan 26 13:26:30 EST 2007 | rw
We are developing a new product that requires conformal coating on the motor controller. We selected a silicone based conformal coat due to its ease of use. There has been disagreement among engineers as to its impact on the motor. We have contact
Electronics Forum | Wed Nov 20 16:47:10 EST 2013 | aaronpavone
I have a right angle male shrouded connector and the whole set of termination leads is tin lead plated, at least 100 microinches thick. Should the entirety of the lead be conformal coated? Or can we have just the joint coated? I know I have coated le
Electronics Forum | Mon Jan 29 20:25:24 EST 2007 | davef
We allow no silicone in our shop, because they ruin solderability.
Electronics Forum | Thu Feb 01 09:46:54 EST 2007 | blnorman
Especially VCM - volatile condensable materials. Strictly verboten around optics.