Electronics Forum | Wed Apr 30 12:26:10 EDT 2008 | dphilbrick
There must be discussions about this on SMTnet but I have yet to find them. I would like to hear from all you smart people about running LF and PB BGA�s on the same board using 63/37 solder. If you run your profile up to peak at around 225C +/- (nitr
Electronics Forum | Sat Jun 25 15:20:03 EDT 2016 | skipper6567
I have a mini/micro transformer that is mounted on a pcb inside my lowrance gps/plotter. I have removed it from the pcb. It has 5 through hole pins, 3 pins out bottom one side and 2 pins out bottom on opposite side. The transformer has yellow tape ar
Electronics Forum | Thu Nov 17 03:34:51 EST 2005 | cangly
Hi, We have a board with over 100 chips (mixed size) and some long Connector DIP through out Wave solder with many issues of no solder and solder bridge, (using clean flux with bubble fluxer and Kester solder bar). Currently we tried to reduce the de
Electronics Forum | Mon Sep 18 19:58:10 EDT 2000 | Dave F
broad answer. There's tons of suppliers. Go to "Circuit Assembly" magazine web site and look-up flux suppliers in the "Buyers Guide." Broad line suppliers are Kester, Alpha ... They will make you answer: I'm joining bla, bla, bla metals, using b
Electronics Forum | Wed Sep 29 08:26:03 EDT 2010 | babe7362000
We are Currently running a Board and it seems that the SOT-223's on the bottom side have flux and water trapped under the part. Nothing has changed in our process and this is the only board that it is happening on. We are using Kester R562 water wa
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so
Electronics Forum | Thu Nov 17 21:46:48 EST 2005 | C. Kolokoy
With DIP type components, a sub-par fluxing method (foaming a no-clean), and a chip wave where one is not needed are formulas for bridging and insufficient wetting. If you have SMD's on the wave solder side of the board greater than 0603, and no SOT
Electronics Forum | Sat Mar 24 07:50:04 EDT 2007 | davef
It's possible that 90/10 is being replaced by LF in many ball suppliers' [Alpha Metals, Kester, AIM] inventories.
Electronics Forum | Thu Dec 01 14:24:25 EST 2005 | Amol Kane
Hi, I am having a SAC 305 solder paste with water soluble flux wetting issue. during reflow, the solder melts, but doesnt flow. the reflow profile was developed by the solder company person (Kester). the board is a test assembly to validate our LF pr
Electronics Forum | Fri Dec 30 16:50:48 EST 2005 | fctassembly
250 tons/month) and, as it has been stated here, many customers have switched from SAC305 to SN100C but we are not aware of any customer who has switched from SN100C to SAC305. As the inventor of SN100C states, �once a customer touches the SN100C, he