Electronics Forum | Thu Aug 28 09:30:20 EDT 2008 | patrickbruneel
Omid, No-clean fluxes need to be used right out of the can without thinning. In the past with RA and RMA fluxes you could adjust or thin them to your desired density because they had plenty of solids up to 30%. No-Clean fluxes have a lot lower solid
Electronics Forum | Thu Aug 28 16:03:08 EDT 2008 | wavemasterlarry
I guess you're adding the gas to keep the fingers clean - sounds likeyou got your threads mixed up on the Forum. Any way I would suggest not doing this. Gas is pretty flammable. I have pix of one our Hollis cleaning machines going up in flames cau
Electronics Forum | Mon Sep 20 12:19:13 EDT 1999 | Brian
| Hi all, | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are TH, the S
Electronics Forum | Wed Aug 27 14:58:21 EDT 2008 | omid_juve
we have problem in setting the density of a no clean flux for using before wave soldering . first we dilute the flux but we have many short circuit problem between the pads of edge connector,then we densify the flux all the short circuit is removed b
Electronics Forum | Tue Sep 21 02:51:06 EDT 1999 | Mohammed saad
Thank you all for your help. about your question Wolfgang, I am using no-clean solder paste from Kester. Mohammed | | Hi all, | | | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we ne
Electronics Forum | Mon Jul 08 08:03:30 EDT 2002 | davef
http://www.goapex.org/html/S32-1_Csonka-Peeren.pdf
Electronics Forum | Fri Sep 05 13:49:04 EDT 2008 | gregoryyork
Tell the board shop to increase the cure temp of the resist as it is undecured especially if you have waxy/greasy resiues on the board and a brown tar like substence in the solder wave itself. If undercured then solder will not flow off the resist pr
Electronics Forum | Wed Feb 26 23:59:48 EST 2003 | Mike Konrad
Grant, No-Clean paste + IPA = White Residue! #1: Stop using IPA #2: Switch to either a solvent-based de-fluxing chemical or an aqueous-based de-fluxing chemical. If you are using an ultrasonic cleaner for your boards as stated, do not use sapon
Electronics Forum | Mon Sep 20 08:21:52 EDT 1999 | Mohammed saad
Hi all, We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. We are producing VGA cards and mother boards for PC's all components to be wave soldered are TH, the SMD is done
Electronics Forum | Thu Aug 28 12:03:54 EDT 2008 | wavemasterlarry
My people said I was needed again here on The Forum. Thanks Mr Head for the goddos on wave soldering. It's a hard process to grasp and not every one nows how to adjust eveything properly. I can tell you regognize expertise when you see it. That s