Electronics Forum | Mon Jul 28 14:30:22 EDT 2008 | grics
Take a look at this. Remember, these are only guidlines and can not replace any paste specs. As Real Chunks said, a profiler will be of HUGE help. We use this to determine what our top side temps are and to see if we have any problems with heat sen
Electronics Forum | Tue Aug 22 14:59:55 EDT 2000 | Mike Naddra
What does the reflow profile look like , the question I had was surrounding the higher reflow temperature and the max temperature that lowest thermal mass components will see. Some other questions that I had were surrounding the components , what of
Electronics Forum | Sat Apr 20 10:12:16 EDT 2002 | davef
If people use an inert gas, they use nitrogen for mass soldering. Inert gases get progressively more expensive as you move down the periodic table. Many times no-clean flux is less active than other flux types. So, people use an inert gas to lower
Electronics Forum | Thu Sep 02 21:02:55 EDT 1999 | Paul Wareham
We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these sizes?
Electronics Forum | Sat May 15 11:27:26 EDT 2010 | davef
We'd expect both OSP poor wetting and improper reflow recipe to show-up in more places than just this one component. But if those are the only choices, we'll go for 'wrong solder paste.' Ooops, that's not one of the choices. Ok, OK, we'll take poo
Electronics Forum | Tue Aug 09 13:25:24 EDT 2005 | pr
From what I can gather, the annular rings are used for grounding when these boards are put in housings. A screw goes through the hole and is torqued down. If there is excess solder on the annular ring, the screw doesn't seat properly. The pallets cov
Electronics Forum | Tue Aug 09 10:38:45 EDT 2005 | SuMoTe
Water soluable dots will wash off after reflow. A water soluable liquid mask will work as well. dots are better for defined (round)holes, whereas the liquid mask works well with odd shapes.
Electronics Forum | Thu Aug 18 13:11:39 EDT 2005 | jsloot
We have our board house apply a peel coat mask that can be brushed off after wave or reflow. You need to brush off while it's still warm.
Electronics Forum | Fri May 14 09:00:35 EDT 2010 | rafacadiz
I attached a RX picture. A lot of voids and micro balls arround the flux residue. What do you think, relow temperature reflow or OSP poor weeting.? I appreciate your comments. Thanks,
Electronics Forum | Wed Aug 10 12:05:11 EDT 2005 | Rob
Hi Pr, No idea what the material is - we haven't usd it for a while now, but it was flush & didn't cause any printing problems on double sided reflow. Your board house should know all about it - I would suggest some but ours are all UK or China/Tai
winsouce.jpg)