Electronics Forum | Mon Dec 02 17:02:28 EST 2002 | Vince Whipple
Steve, I agree with the recommendation to check the temperature. This is the first place to go. Is this an IPA or water based Noclean? What is the topside temp of the assembly at the effected areas? If you are too cold you will have a tendency to hav
Electronics Forum | Fri Dec 06 18:13:15 EST 2002 | slthomas
We only have solder balling problems in the interface of the pcb with the selective soldering pallet. All other boards (single, and double sided glue and waved alike) are fine, so I'm not thinking this is going to follow the normal path for resoluti
Electronics Forum | Sat Feb 20 09:56:22 EST 1999 | Tufty
| We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not b
Electronics Forum | Thu Dec 05 11:36:30 EST 2002 | William Guatemala
Have you check the flux gravity lately? If not, Check the flux gravity every 6 hours to make sure proper parameters are meet. Here is a list of things that may cause your solder ball problems; Excecive heat, defective fixtures, preheating temperature
Electronics Forum | Mon Dec 02 16:19:11 EST 2002 | slthomas
Unfortunately it's nc or we'd be worrying about this on the fly. Non-contact is defintely and issue....this is an 18"x9" board with 1500 bottom side SMT parts that are scattered among the through-hole and vice-versa. We're currently using 7 hold-
Electronics Forum | Wed Dec 04 09:24:52 EST 2002 | jseagle
I have found that preheating the solder pallets prior to use helps cut down on the solder balling. Also, we do not cool the pallets between passes and we use a spray fluxer because a hot pallet will knock down the head on a foam fluxer. We use WS f
Electronics Forum | Mon Dec 02 16:01:15 EST 2002 | russ
If you can, attach athermocouple to the locations where you are getting solder balls. A previous product I had showed the same thing and we found that we had inadequate preheat leaving the liquid flux to splatter when it hit the wave. It could aslo
Electronics Forum | Mon Dec 02 12:52:40 EST 2002 | slthomas
We're trying a selective soldering pallet for the first time with mixed reviews. Are solder balls a prevalent problem with this process? Most of them seem to correspond with pallet wall locations....is it too much turbulence from the rotary chip wav
Electronics Forum | Mon Dec 02 13:16:31 EST 2002 | kenBliss
Hi Steve The people who will have the answer is the experts at EMC Global Technologies. They know their stuff, they are the leader in the solder pallet industry. They design and build them to work right. http://www.emcgti.com for contact info. Hop
Electronics Forum | Mon Dec 02 18:01:12 EST 2002 | GSW
Hi, Try to check if there is water absorbed in the flux or the humidity around the wave area. possibly plating on barrels that might be damaged?