Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Tue Jun 16 15:01:58 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Tue Jun 16 15:00:12 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Thu Feb 10 16:00:31 EST 2000 | Travis Slaughter
I have had cases when it was necessary to run epoxy and paste at the same time. The only good reason I know of to even think about messing with going to this trouble is if the surface tension of the solder melting pulls the part out of alignment. T
Electronics Forum | Mon Aug 24 03:59:26 EDT 2009 | hurr
Hallo Joanne, I had employed by producer of Ecofrec 303. We make many tests of corrosion and conductive test in our company. All results of this tests was OK . Vast majority correspond mil standarts. When I ask my labor assistent in BRY, white residu
Electronics Forum | Fri Mar 26 15:17:30 EDT 2010 | jooh
Thanks for your replies! So what I understand is that ICT in reality is "only" a production process safety net, but it's a net that in most practical cases is needed. What ICT can not catch is (all) bad solder joints. What are the methods to find t
Electronics Forum | Mon Mar 29 12:10:14 EDT 2010 | rway
Test Jet will work for catching lifted leads, certainly. X-ray is the only thing for testing for internal solder defects such as voids and cracks. I personally do not have any experience using X-ray, so I cannot advise on its reliability. Perhaps
Electronics Forum | Fri Jun 29 14:15:00 EDT 2001 | stefo
This is a question about complying with J-STD-001 solderability testing. Do any of you have your vendors certify that the components and PCB's that you buy from them comply with the solderabilty requirements spelled out in the -002 and -003, in lieu
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
.gif)