Electronics Forum | Fri Jan 03 12:12:22 EST 2003 | richard
Good day and thanks for your comments Mike, What did I understood from your notes� 1) ROSE test (�extracting solution�) is probably good enough (with good equipment) to penetrate the space under my micro BGA. 2) I should test 2 parallel batches of
Electronics Forum | Sun Jul 29 09:17:20 EDT 2001 | davef
Tough to say, but ... Chlorine: Many fluxes contain chlorine. Sulphur: Many solders and paper packing materials contain sulphur. Sodium: No idea. IPC-J-001 talks to board cleanliness and specifies criteria according to the cleanliness test met
Electronics Forum | Fri Jun 05 10:24:56 EDT 1998 | Earl Moon
| I have just been assigned to look into the ionic chromotograhy test on our PCBA but I have zero knowledge. Could anyone help to explain what is this test about? Is it | a) a destructive test? | b) What is the measurement unit of this test? | c) Wh
Electronics Forum | Fri Dec 01 16:02:33 EST 2000 | Jim M
Thanks for your reply. I 've tried to clarify and answer your questions. The water soluble paste used is WS3060, type 4. The boards are sent through a inline di cleaner after reflow. There is a hot Di waterwash, rinse and then hot air to dry the wa
Electronics Forum | Mon Oct 22 16:47:09 EDT 2012 | edmundo
We use a NC Flux in the wave solder and after aAcelerated Life Test cicle we found contamination white residues paths between some solder points. Does somebody know a possible cause for this contamination.
Electronics Forum | Thu Jun 26 17:40:21 EDT 2003 | Steve
Wanted to inquire if anyone has a way to monitor cleanliness of boards that are assembled with a no-clean process. I'm aware that incoming board cleanliness can be monitored, however, I am after checking of cleanliness of boards after assembly. Wit
Electronics Forum | Sun Feb 26 21:48:28 EST 2006 | Mike Konrad
Hi GS, Just a clarification� No-clean does NOT equal no ions. It equals less ions (at best). Automatic R.O.S.E (Resistivity Of Solvent Extract) testers are commonly used to detect ionic contamination from no-clean applications. Your comment rega
Electronics Forum | Tue May 18 22:31:05 EDT 2004 | davef
Ionic cleanliness is pretty much meaningless, when discussing nc flux residues. If you do the good solder routine and measure the boards, you'll be in the out-house, because the water in your resistivity of solvent extract tester will turn the res o
Electronics Forum | Tue Aug 16 00:27:12 EDT 2005 | Peter
Hello, I have a question on white residues formation at wave soldering. We have recently run experiments to test the performance of various halide-free water soluble fluxes (ORH0 under JSTD-004). The flux was applied through a spray fluxer and all P
Electronics Forum | Wed Aug 17 14:18:11 EDT 2005 | ppwlee
Dave, Answers to your questions: * From your pictures, the white residue appears to be only on the solder mask. Is that correct? If not, what is the location [eg, solder, nonsolder/nonmask areas] of the residue that doesn't show well in the pictur