Electronics Forum | Tue Jul 31 10:41:49 EDT 2001 | ronho
I'm interested in process information from someone who has experience with this package, such as pad design, stencil aperture dimensions, stencil thickness, unique issues, profiling, solder paste. Design is considering this package for future produc
Electronics Forum | Mon May 31 19:20:50 EDT 1999 | Raeto Zryd
I have difficulty to convince my management to air-condition our manufacturing facilities. The room temperature fluxuates from 8 deg.C in the morning to 25 deg. C in the afternoon. The PCB topside temperatures in the reflow oven and wave soldering ma
Electronics Forum | Thu Apr 29 19:52:32 EDT 1999 | WinTech mfg
I would like to know if there is any good training for Hand Soldering, Component Identification, Wave Soldering, and so on. I have seen two diffenent tapes and they were short and poorly done, I would like to buy some if I knew it had some good Trai
Electronics Forum | Wed Apr 28 14:17:20 EDT 1999 | Bob Willis
| Anyone using hot air nife for wave soldering process. | Does it work? | Does it really eliminate solder bridging and does it create any other problems? | | any feed back will be much appriciated. | | Thanks | | Tony A | | I have a article I p
Electronics Forum | Wed Apr 28 14:17:32 EDT 1999 | Bob Willis
| Anyone using hot air nife for wave soldering process. | Does it work? | Does it really eliminate solder bridging and does it create any other problems? | | any feed back will be much appriciated. | | Thanks | | Tony A | | I have a article I p
Electronics Forum | Fri Apr 23 11:31:35 EDT 1999 | J.J. Thomas
A customer told me that pad geometry was to be different depending on soldering process. I think this is untrue. What is stated in the IPC - SM -782 standards is that parts should be placed to elimanate a trailing edge. This however should not e
Electronics Forum | Sun Mar 28 17:05:13 EST 1999 | Glenn Peters
I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. What disadvantages are there when using this flux? Do you have any contact details with any o
Electronics Forum | Sat Mar 20 10:40:01 EST 1999 | greg cronin
I am looking for clip art images of electronics assembly. Images like wave soldering, surface mount components, soldering irons... just general assembly graphics. Many sites have different individual images that they use I was just wondering if any
Electronics Forum | Fri Feb 05 17:56:38 EST 1999 | Chad Haim
| I realize it's been discussed many times before. I need to know your opinions, experience, and knowledge concerning "today's"/latest and best pallet designs, suppliers, and methods for using them more effectively. | | Thanks much, | | Earl Moon |
Electronics Forum | Thu Aug 06 03:57:59 EDT 1998 | STONEY TSAI
Hi, friends, The gold plating and HASL boards made some difference on solderability for both reflow and wave soldering processes. It is difficult to investigate the interactions between raw materials and process parameters setting. Anyone provides th