Electronics Forum | Tue Aug 09 12:09:26 EDT 2005 | mtd
I am having reflow issues with small 6 pin SOT's. The joints on these components still look like solder paste after the reflow oven. I have tried adjusting the profile on forced air oven. Any recommendations as what to change in the profile or proces
Electronics Forum | Mon Aug 15 05:57:47 EDT 2005 | www.teiloengineering.com
we are manufacturers and suppliers of titanium retrofit kits for all type of wave solder machines as you will see on our website best regards robert emmanuel
Electronics Forum | Wed Aug 17 13:57:27 EDT 2005 | ppwlee
We have encountered what appears to be mask discoloration after wave soldering. The areas of concern coincide with the areas that were exposed selectively by fixtures during wave soldering, dominated by one date code of PCB with a slightly different
Electronics Forum | Tue Aug 30 12:06:41 EDT 2005 | MM
All of your response were similar to our investigation. Paste was sufficient, pcb's and parts came from several different lots run in at least 2 seperate ovens. Joints look good but the solder is soft?
Electronics Forum | Wed Aug 24 09:42:23 EDT 2005 | james
That is what I was looking for. The profiles did not make much sense to me. We are getting alot of cold solder joints or bumpy solder joints.
Electronics Forum | Mon Aug 29 18:16:13 EDT 2005 | RoHS Ron
Has anyone heard of IET (ietechnologies.net) and the wave solder machine they are offering? It's an Asian made, leadfree ready machine that looks fairly robust and I understand that the cost is close to 1/2 of what you would pay for one of the big 3
Electronics Forum | Thu Sep 01 10:44:32 EDT 2005 | Clampron
Hi Slaine, Actually, HMP Leaded solder is not complient, it is exempt only when the specific application requires this temp. Sorry for the intrusion but I am working on something very similar currently. Thanks Chris
Electronics Forum | Fri Sep 02 06:47:17 EDT 2005 | dougs
Is there a standard that we should aim for in respect to the strenght of the solder on SMT leads? We have a customer who are testing our product by pulling leads off of pads then returning them.
Electronics Forum | Fri Sep 02 10:10:54 EDT 2005 | Mity-C
We had a customer who came in to discuss a solder adheasion problem on some sub-assemblies we were building for them. When they arrived, they put a sub assembly in a vise and hit it with a hammer. I was speechless to say the least...... C
Electronics Forum | Thu Sep 08 09:47:20 EDT 2005 | lupo
I will try with temperature 255 C degrees. The wetting force vs. solder temperature for SAC305 is more than 265 C degrees (the temperature of trials). Thanks for the advise. Regards