Electronics Forum | Fri May 15 10:51:12 EDT 1998 | Justin Medernach
| We understand that testing for ionic contamination and surface insulation resistance measure different properties. We assemble printed circuit boards for other companies. We will not get combs on 90% of the boards that we assemble. | We have no c
Electronics Forum | Tue Apr 07 15:55:37 EDT 1998 | Michael Allen
| I'm also in the "Don't score it" camp. Routed breakaways are much better. If your wave solder process has decent control on the wave height, you shouldn't worry about flooding the boards. | The fine pitch consideration for panelizing - Since you
Electronics Forum | Sun Mar 15 23:58:01 EST 1998 | Phill Hunter
| | I am having a problem with Entek coated boards. The solder past seem to just ball up on the pads. I had no problems with the board when it was hot air leveled. The board is double sided surface mount. I have tried adjusting the oven profiles m
Electronics Forum | Fri Mar 06 15:04:11 EST 1998 | Todd N
| We have a double sided pcb that is surface mount on both sides. Now a Through Hole connector has been added. Appart from hand soldering does anyone have info. on reflow soldering the part. The connector is 0.1mm pitch, square legs. | 1) Do you need
Electronics Forum | Fri Mar 06 23:02:43 EST 1998 | Scott McKee
| | We have a double sided pcb that is surface mount on both sides. Now a Through Hole connector has been added. Appart from hand soldering does anyone have info. on reflow soldering the part. The connector is 0.1mm pitch, square legs. | | 1) Do you
Electronics Forum | Thu Feb 19 12:45:05 EST 1998 | Earl Moon
| I have an Electrovert Ultrapak 445 Wavesolder machine with 3 IR preheat zones and a single wave with omega wave. | I want to run a DOE (Taguchi) to determine the optimum settings for soldering both single-sided and | double-sided boards. Can any
Electronics Forum | Tue Aug 28 16:41:42 EDT 2001 | davef
Very few concern themselves about the strength of solder connections, because it doesn�t require much strength to keep a solder connection attached to the board. More important are factors that arise as a result of the different materials properties
Electronics Forum | Fri Aug 24 19:08:17 EDT 2001 | stefo
Happy Friday All! Well, it seems another "opportunity" has presented itself to me. Looking to assemble a 24" X 24", 52-layer board... piece-o-cake, right? Not real sure of all the components that are on it, but I do know that there is some 20-mil
Electronics Forum | Fri Oct 26 17:01:52 EDT 2001 | davef
We process no Teflon boards. Companies, such as Rogers and Taconic, make laminates of Polytetrafluoroethylene [PTFE] er �Teflon�. Common �Teflon� laminates are: * Woven glass / PTFE * Random microfiber glass / PTFE * Ceramic / PTFE * Woven glass /
Electronics Forum | Wed Nov 07 17:11:14 EST 2001 | davef
1 CAN WAVE SOLDER AFFECT OR DAMAGE BGA? Sure. Since you are vague, assuming: * Partially assembled board was not stored to prevent moisture absorption. * BGA is in a plastic package. * Partially assembled board was stored long enough to exceed th