Electronics Forum | Tue Nov 01 20:48:53 EST 2005 | erokc
I am forced to use fine pitch parts in a new design. Board alignment in production has to be addressed. Fudicals, where to place, shape, size. I'm assuming they must be in the copper to represent the pad positions. Are they placement machine depe
Electronics Forum | Mon Dec 12 00:52:24 EST 2005 | cindyleng
Dear Greg, We can manufactured various of Metal squeegee blades, pls give me email address, i'll send the picture to you. Tks and B.Rds Cindy Leng HWATALI TECHNOLOGY (HK) CO TEL: 86-755-83016463 FAX: 86-755-83016648 Email: hwatali88@yahoo.com.cn
Electronics Forum | Tue Feb 07 11:52:06 EST 2006 | slaine
Hi not bought fans from them ive sent failed ones off (usually siezed solid) and had them reconditioned. Theve run with no problems. Address of Furness Winding Co Ltd Kings Works Kings Road Ulverston Cumbria LA12 0BT Telephone and fax Tel: (01229)
Electronics Forum | Sun Mar 12 11:55:52 EST 2006 | ravi
Hi Amol, I am ravi from Autron India PVt Ltd, we are business partner with PVA, i would like to know your company address & ur e-mail ID , so that we can start communication officially. My e-mail Id --ravi@autroncorp.com. With Best Regards Ravi
Electronics Forum | Mon Apr 03 10:18:50 EDT 2006 | amol_kane
Hi Smartasp, would you mind giving the name/ more info of the company you work for? (this is not related to the post and hence we can take it offline if you want). my e-mail address is amol_kane@hotmail.com I am originally from India, and hence inte
Electronics Forum | Wed Jul 19 15:14:57 EDT 2006 | cuculi54986@yahoo.com
We have SnCuCo (Cobalt 995) solder from MRI in our solder pot. I'm not the wave master here, but I believe our wave master is pretty satisfied with it. Send an email to cuculi54986@yahoo.com, and I'll forward your email address from there to him.
Electronics Forum | Mon Jul 24 11:35:42 EDT 2006 | Jimk@ics-inc.org
We have experienced a problem with tin leaching or discoloration of lead terminals on random parts on solder side of a paste/paste operation. The profile has been used on previous production runs and there doesn't appear to be any heat damage to othe
Electronics Forum | Thu Sep 21 08:06:15 EDT 2006 | bobpan
I think 365 is ok. You should check and make sure the z-rod's spring is ok. Just make sure it is not sticking. Dont waste your money on the pm. If you want a complete list of things to do.....leave an e-mail address and i can e-mail you a list.
Electronics Forum | Fri Sep 22 09:17:17 EDT 2006 | Roland Girouard
Thank you for your input -good timing! We here at SMTnet had a meeting yesterday to discuss the forum speed issues so we will be addressing that concern soon. We'd appeciate any other feedback, suggestions and/or functionality requests you have. Ro
Electronics Forum | Thu Jan 11 09:23:32 EST 2007 | mscalzo3
BE, Flux coating helps as there is no solvent to volatize. Also, we offer vacuum-cast preforms that will eliminate the possibility of the voids comimg from the alloy itself. I can email a PDF of some profiles, all I need your email address. You c