Electronics Forum | Thu Dec 12 07:37:13 EST 2002 | davef
Immersion plating appears like electroless, sorta, but is different chemically. Plating is converting metal ions in solution to metal on the board. Those metal ions are "converted" by adding electrons to them. The source of these electrons defines
Electronics Forum | Fri Jun 03 16:52:48 EDT 2005 | davef
Your customer is being smart. When we look at the evaluation that some component suppliers do in assessing the potential of the pure tin solderability protection they've chosen to produce tin whiskers, we just shake our heads. Essentally they say,
Electronics Forum | Fri Oct 28 21:46:35 EDT 2011 | rdh_41
Hi , I'm interested in Tin and hoping to open long-term business relationship with your company. We are Taiwan-based company dedicate in Tin (Sn). We are looking for opportunity to work with you. And it would be great if you have large quantity of t
Electronics Forum | Fri Oct 13 17:21:05 EDT 2000 | Jason Nipper
A few weeks back we experienced a wave process problem where we received deposits on our pcb. At first we though it was dedrites but after an outside analysis of the deposits they were found to be tin. We have tried to remove the deposits with brus
Electronics Forum | Sat Aug 21 12:13:17 EDT 1999 | Brian
| I am being asked, by my vendor and Purchasing people about converting from Tin/lead pads on P.C.B's to Electroless Tin Plating. | Can any one tell me what I have to change in my SMT | process (paste, reflow, etc) If any? | I ran one P.C.Boar
Electronics Forum | Tue Jun 29 18:35:59 EDT 1999 | JohnW
| | Could somebody tell me what means Leaching, ie: "Leaching of terminal end face exposing the ceramic"? | | | Roberto: Leaching, according to the SMTnet Library of Terms: | | Leaching. Dissolution of a metal coating into liquid solder. Nickel ba
Electronics Forum | Mon Apr 26 11:04:53 EDT 1999 | Dave F
| | Earl said, in essence: | | | | | Justin is absolutely right ... | | | | | | Again, Entek is not much more than a flux coating ... | | | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those coatings chemi
Electronics Forum | Mon Oct 19 13:32:06 EDT 1998 | Mark Schwarz
| How are solder pastes manufactured right from the level of extracting lead and tin ? | | | The Tin Institute is good but I rarely find that the raw metals industries guys know about pastes. Making a tin-lead alloy for pastes, as for raw bars, is
Electronics Forum | Mon Oct 08 23:17:48 EDT 2001 | Brad Arnold
We are trying to produce a PC Card bus assembly with a 672 pin BGA on one side. These pcb's are .015 thick. I believe the ball pitch is .5mm. The pcb's are plated with white tin. The pcb's are in a 1 X 3 array. We had 2 plates with appropriate cutout
Electronics Forum | Wed Dec 12 07:38:04 EST 2001 | smtspecialist
I have observed the same thing with solder composition in this case I am using 63/37 NC which is giving good results usualy. The liquid tin, product from MG Chemical that I used is to tinplates copper circuit on PC boards. I tried on few relays, it