Electronics Forum | Tue Apr 29 03:29:01 EDT 2003 | chrissieneale
Does anyone have any figures on visual fail / no pick? our machine records this but no one has been recording the machine and it's been running since we've had it (a good few years). I am currently assuming it's about 0.2/0.3% but this is a (not very
Electronics Forum | Tue Apr 29 07:12:49 EDT 2003 | Glen barden
Sn/Cu/Ni is introducted to me in wavesoldering lead free process. Around in our industry, we have a plenty of info. about SAC but not on this alloy. The distributor showed me some information about this alloy including less dross, more shiny /smoot
Electronics Forum | Wed Apr 30 12:30:14 EDT 2003 | Guillermo
Hello, I would like to ask for cooments/advices about the inspection of small solder deposits inspection (aprox 4 mills). We tried with X ray and Scanning acoustic microscope but it looks like due to the small size, we could not be sure to get all t
Electronics Forum | Thu May 01 18:37:31 EDT 2003 | gregoryyork
Did you get any dulling of the solder joints at all or importantly was the resist discoloured or bleached after cleaning. It is possible to absorb flux and saponifier into the resist and this will definately cause poor SIR or electromigration especia
Electronics Forum | Tue May 06 14:52:37 EDT 2003 | bremerg
Pictures are now located at http://www.stevezeva.homestead.com/ These components are 2W resistors that only see 1/2W at max. during normal use. I have contacted IRC still wqaiting for a response. The resistors were tested as good. But the circuit
Electronics Forum | Wed Jul 16 09:55:05 EDT 2003 | swagner
To answer the first post after my initial response we haven't published any of our lead free data since it is proprietary, sorry. As for the nitrogen cabinet it has been proven that over time the Gold plating can build up a layer of oxides that can
Electronics Forum | Mon May 05 22:24:17 EDT 2003 | jlipton
We are investigating a system, using 2-D matrix code, that will identify and track every PCB throughout our factory, starting from bare board. As a low-medium volume manufacturer, would labels or laser marking be more cost-effective? How difficult is
Electronics Forum | Fri May 09 16:48:59 EDT 2003 | Ozzy
KH This won't work if your planning on running these 2 machines together in line. The fast machine will always be waiting on the slow machine. How many Philips FCM's have you seen in line with Mydata? Don't think to hard; the answer is zero. Wh
Electronics Forum | Wed May 07 09:02:29 EDT 2003 | cyber_wolf
I was wondering if anyone has done a study on thermo couple attachment with light cure adhesive.I have read all the papers and articles about aluminum tape, Kapton, and high temp solder.I have yet to hear anything regarding the accuracy of light cure
Electronics Forum | Wed May 07 11:31:21 EDT 2003 | cyber_wolf
Well Dave, Check the number that is on your adhesive tube. They make several different types of adhesives for use on different substrates. The rep from Dymax recommended the 3073 for bonding to FR4. We use a Dymax HHL400 handheld curing light. Click
.gif)