Electronics Forum | Fri Mar 04 01:08:19 EST 2011 | kemasta
Thanks davef Bridging:- There is no heat sink on the BGA, the heat sink will be fix after relow. I do believe paste had something to do with it, but currently this defect didn't appear so oftenly, so we think that the main root cause is not from the
Electronics Forum | Wed Jan 14 10:07:38 EST 2004 | Patrick
More on QFP soldering issue as per Paul f original e-mail. 1. Problems occured on different PCB's, on different lines using different equipment 2. Flux residue is common in the dimple on the solder. 3. The fault occurred using both "Kester 265" & "Al
Electronics Forum | Mon Dec 25 08:43:35 EST 2017 | arjunkolavara
Hi , We are having Pin hole issues on the passive locations in the board after the SMT reflow process. Details: PCB surface Finish : ENIG . Solder paste : Alpha OM338 – M13 / Indium SMQ92J Location : Its Random and more on passive components. {
Electronics Forum | Thu Dec 28 16:20:12 EST 2017 | rgduval
Pictures of your issues would help us to help you. Pin holes/blow holes are generally caused by either moisture or flux volatiles/organics. Since you've virtually eliminated moisture, it might be time to look at your paste/flux. You can call eithe
Electronics Forum | Wed Dec 19 09:56:20 EST 2001 | guicho_v
I'm new in SMT world, and I've got my 1st challenge: I'm having de-wetting issues with a specific IC 160 pins MQFP (six location, failure is random), where one pin has de-wetting (solder reflow OK, and there is evidence of having contact the past and
Electronics Forum | Mon Nov 20 13:35:52 EST 2006 | cuculi54986@yahoo.com
We evaluated the OM338 from Alpha and it worked great! Looked like crap, though, compared to the other products out there. When I set the boards out in front of the Alpha sales guy to show him the difference in appearance between his boards and the
Electronics Forum | Fri May 14 12:01:40 EDT 1999 | Chrys Shea
| | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | | Thanks | |
Electronics Forum | Fri May 14 14:52:56 EDT 1999 | Ryan Jennens
| | | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | | | | T
Electronics Forum | Sat Jan 06 22:09:53 EST 2001 | Greenman
Cory, I've got a lot of experience of testing of this type. The physical (not chemical) nature of the flux residues is the crucial issue in compatibility. If you have a softer residue (either caused by a thick initial solder paste deposit, or a low p
Electronics Forum | Thu Mar 08 12:40:54 EST 2001 | Ralph Merk
We are currently using 0402 resistors and capacitors in our production process. Our equipment is as follows: - DEK 265 - Siemens S25/F5 - Vitronics XPM520(5 zones) - 2% silver solder Alpha WS678 The problem is that randomly some 0402 capacitors are