Electronics Forum | Thu Dec 10 09:06:47 EST 2009 | stepheniii
Just how cold do you store your paste? And what are your solder paste reps like? Here they fall over each other giving support for their paste. And have you seen the problem with flux separation or have you only heard about it?
Electronics Forum | Mon Jan 09 23:24:47 EST 2017 | saju86ece
Hi, We are doing pin in paste reflow process in one our product ( but paste printed on bottom side of the board and top side will be assembled through hole component)in which faced cold solder issue in THT capacitor location after reflow. The solder
Electronics Forum | Wed Jul 27 09:58:05 EDT 2011 | davef
Pressure printing systems Conventional stencil printing techniques have fundamental limitations as regards paste handling: The volume of paste available for printing is limited, so frequent replenishment is necessary Paste is difficult to c
Electronics Forum | Wed Apr 21 12:03:59 EDT 1999 | Michael N.
I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is about
Electronics Forum | Sat Dec 18 15:23:05 EST 2004 | grayman
We used to add flux on a "expired" solder paste but we discontinued as there are many problems and customers complaints coming from our American customer. Like unwetted solder pads,dull and cold solder and many others. The profit is really ok but qua
Electronics Forum | Wed Apr 21 22:15:12 EDT 1999 | Chris
| I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is abo
Electronics Forum | Fri May 29 08:25:13 EDT 2009 | floydf
We are getting what looks like cold solder joints on one of our boards. The boards have an aluminum substrate, and use OSP plating. The solder is lead free - 96.5 Sn, 3.0 Ag, .5 Cu. The flux is no clean. When we first had the problem, my solder profi
Electronics Forum | Fri Apr 29 08:39:01 EDT 2005 | davef
Few solder paste suppliers recommend freezing solder paste. Check with your supplier for recommendations. Examples are: * In many cases, nothing happens. However, some pastes are susceptible to damage that impairs paste performance. As a consequenc
Electronics Forum | Wed Apr 21 20:50:26 EDT 1999 | Dave F
| I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is abo
Electronics Forum | Wed Jan 14 00:02:10 EST 1998 | jerry
I have a problem! The solder on my pc boards look great comeing out of my reflow oven. They go thrue the rest of the prossese and at the end at the qc station it's cold or whitish or gray not shiny. does any one have a idea on how to correct this pro