Electronics Forum | Thu Sep 20 07:18:42 EDT 2018 | proceng1
Has anyone else been experiencing this lately? We have had a rash of boards that come in properly vacuum sealed. We store them in the hot room until we are ready to build, and we get bubbles under the solder mask. We've had 4 different jobs, all di
Electronics Forum | Fri Jun 19 09:45:21 EDT 1998 | Mike Cox
Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. Mike
Electronics Forum | Wed Jun 28 16:16:09 EDT 2006 | Gman
Good article. Would EDX analysis of the cross-section at the void joints be a good method to determine any plating contamination or solder mask issues?
Electronics Forum | Thu Nov 01 10:57:34 EDT 2012 | kris1128
Has anyone heard whether the elevation of a plant can effect solder joint formation? One plant at sea level, one at 7,000 feet elevation... same equipment and profiles, big voiding defects at higher elevation. I did a search and found no similar post
Electronics Forum | Fri Nov 03 07:28:27 EST 2006 | davef
Via filling methods are: * Tenting * Plugging * Capping * Flooding Tented Via. A via covered with dry film soldermask; the via is not filled. When tenting from both sides there may be issues with trapped air that expands during mass soldering. Plug
Electronics Forum | Wed Jun 05 17:13:58 EDT 2002 | Yannick
Hello! I have a strage problem, we made some production with uBGA, BGA, 0201, 0805, and other type of component. We didn't put the uBGA and 0201 and BGA on the board at the end of the line we look a our solder joint and surprise the solder made a
Electronics Forum | Wed Mar 12 16:30:45 EDT 2008 | operator
I witnessed this at our sister company. It seems to be their standard process. It is not my place to interfere with their processes. I was just curious if there was any chance of brittle solder joints or other defects that might be caused from the WS
Electronics Forum | Sat Nov 03 11:08:24 EDT 2012 | anvil1021
We have experience with this alloy, but with enig and we did start with PB HASL, none of our PCBs would of course pass thermal cycling at normal temperatures with the HASL so we went to ENIG. we could thermal cycle at 100-115C with no issues. We foun
Electronics Forum | Wed Nov 06 05:13:01 EST 2002 | Dreamsniper
Crystalline flux if it is really clear should not be a problem. We were using Amtech paste before and we have the same results. Sometimes we mistakenly see it as a dry joint because of the reflections from the lighting of our Metcal inspection system
Electronics Forum | Wed Sep 10 12:56:09 EDT 2003 | davef
Intermetallic compounds [IMC]: * Form during the alloying process of some metals. In soldering these are Sn, Ni, Ag, Cu, Au. * Do not accept solder. * Increase in depth in logarithmic proportion to both time and temperature. [So during the solder