Electronics Forum | Fri Oct 19 11:51:25 EDT 2007 | rgduval
By definition, no clean solder can be not-cleaned. The solder/flux are formulated to result in low ionic-contamination, hence, no cleaning. I have, however, always had at least one customer that requests their no-clean solder get cleaned. No-clean
Electronics Forum | Thu Jan 18 15:28:10 EST 2007 | CK the Flip
If you are, in fact, running a No-Clean solder paste: Different no-clean solder pastes will leave different types of (benign) residues. If your paste has been qualified from a Bellcore/SIR/Electromigration standpoint, any residues remaining will NO
Electronics Forum | Wed Sep 04 23:55:10 EDT 2002 | jersbo
aight... Ive read the SMT archives... Ive got issues,,, 25 boards WS boards with NC on them HOw do I clean them? Used Everkleen in Prewash and wash in a dishwasher , cleaned most of the NC flux off but I have residuals. especially on the fine pitch
Electronics Forum | Thu Jan 18 12:30:19 EST 2007 | slthomas
Change pastes, although insufficient heating may leave excessive residues. Is this on one board or all products? No Clean or water soluble? Do you profile accurately or "guesstimate" your settings?
Electronics Forum | Thu Sep 05 18:15:15 EDT 2002 | pjc
There are chemistries out there that will solublize some post-solder NC flux residues. I have had success with Zestron material Vigon A200 and Petroferm material Hydrex DX. Go to http://www.zestron.com and http://www.petroferm.com These are chemical
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Tue Aug 10 03:13:30 EDT 1999 | Dreamsniper
| hello to everybody, | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | does anybody know how to eliminate flux residues or how not to produce them during rework operatio
Electronics Forum | Tue Aug 10 05:51:03 EDT 1999 | Gian.D
| | hello to everybody, | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | does anybody know how to eliminate flux residues or how not to produce them during rework op
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Mon Oct 22 15:41:39 EDT 2007 | davef
Bruno The real question about your troop using Kester 951 wave solder flux on boards is: how is the flux applied and controlled. See, when you apply this flux with your wave solder fluxer, it is ideally applied in a metered fashion with your fluxer