Electronics Forum | Mon Feb 18 17:36:32 EST 2008 | kennyg
I should have mentioned... the only flux we use for the hand soldering is wire-core, no bottle flux. I think it should be a non-issue to leave the activated wire core flux residue. I'm just looking for some way to prove it to the designer.
Electronics Forum | Mon May 15 10:16:36 EDT 2006 | slaine
Hi Im trying to find a supplier for 30swg HMP solder wire idealy the alloy I want is 93.5Pb, 5Sn, 1.5Ag, 296 to 301 degrees C. Flux cored. 30swg or 0.3mm diamiter. but the critcal parts are the diameter and the melting point, 300 degrees +-20 degree
Electronics Forum | Tue Feb 19 08:49:34 EST 2008 | rgduval
Get the ionic specs from your flux manufacturer, and show it to the designer. No-clean flux/solder is supposed to be low to minimal in ionic contamination, which allow the whole no-clean thing. If he needs further proof, you can have the board io
Electronics Forum | Mon Feb 18 17:27:13 EST 2008 | jdumont
If the hand soldering is done right and you use little to no extra flux (other than whats in the solder wire) you should be ok. You should still verify with some testing however... You need to make sure any flux used is activated, thus rendered benig
Electronics Forum | Thu Aug 20 14:52:40 EDT 2009 | davef
Armando: We're guessing that the white residue is on the laminate also. We believe that the residue has something to do with your low residue flux and water. It could be: * Water contamination in the flux. * Poor selection of preheat temperature that
Electronics Forum | Fri Jan 21 13:57:52 EST 2005 | saragorcos
Hi esoderberg - I was wondering if you had tried altering your soldering profile to try and fully solublize the no clean flux residues and elimate your cleaning dilemma? You can check out my company's website if you want some free reference material
Electronics Forum | Fri Jan 21 08:00:09 EST 2005 | Lloyd
I recently saw a brief presentation on selective cleaning using Co2. In basic terms a fine jet of Co2 is blasted onto the desired area of the PCB removing the contamination and supposedly causing no damage to PCB or components. I think it's quite a n
Electronics Forum | Mon Sep 28 09:35:28 EDT 1998 | Clive Heke
I have had some field failures returned recently, the boards had flux contamination under the components in a sensitive area, Nothing really visible until the component was removed, and the board had no evidence of rework of any type. Is it possib
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink