Electronics Forum | Tue May 25 12:19:55 EDT 1999 | M Cox
| | | | | | | | | Any suggestions on how to maintain Adhesive dispensing nozzles??? They seem to plug up over night and it is starting to get on my nerves. We have tried leaving the nozzles in the machine, removing them and soaking in alcohol, bl
Electronics Forum | Wed May 26 10:00:03 EDT 1999 | David Scott
| | | | | | | | | | | | Any suggestions on how to maintain Adhesive dispensing nozzles??? They seem to plug up over night and it is starting to get on my nerves. We have tried leaving the nozzles in the machine, removing them and soaking in alcoh
Electronics Forum | Mon May 16 22:59:40 EDT 2005 | davef
We believe your problem is caused by the mismatch in CTE of the material ised in your BGA. In fact, this "potato chipping" [where the corners curl-up] is present in all BGA. The issue is the matter of degree. [Mismatching CTE is how old thermostats
Electronics Forum | Wed Jun 25 12:20:03 EDT 2003 | russ
This may make it easy, Do you really need soak? Or can you just ramp to reflow. Most pastes that I am aware of perform just as well using the linear ramp as opposed to the ramp/soak /spike. Now, out of curiosity how are you attaching the thermocou
Electronics Forum | Thu Jun 26 04:34:49 EDT 2003 | emeto
Hi James, I saw very good posts here.Now I will give you one more practical way: 1. My advice is to encrease the temperature(like your first sidgestion). Termostress is important thing so your first zone should be 120-150C. 2. The paste profile. If
Electronics Forum | Wed Jun 25 18:17:48 EDT 2003 | Brian W.
Water soluble pastes generally work best with a ramp-to-spike reflow profile. Check your paste manufacturer's recommended profile. There are many factors that impact your profile; board thickness, component density, buried thermal masses, board si
Electronics Forum | Tue Jun 17 07:17:09 EDT 2003 | James
The main problem I am having is getting the Rising slope 1-3 degrees. If I slow the conveyor down then I have too long of a reflow and if I speed it up then my ramp rate is too high. I was not sure if I need my first zones at a low temp or higher t
Electronics Forum | Thu Jun 26 09:50:05 EDT 2003 | James
To Brian W. I think I will use your concept thanks for the help and from all the others that gave me suggestions. I seem to get best results from a Low temp at first with hardly no soak and just a ramp to spike. Thanks again.
Electronics Forum | Mon Jun 16 13:57:48 EDT 2003 | James
Could anyone give me a basic profile temperature settings for a conceptronics 7 zone oven and speed? I have the first couple of zones ramped up to get to the soak temperatures. Is this correct or should I start out with low temperatures and graduall
Electronics Forum | Tue Jun 24 14:13:51 EDT 2003 | James
So which one is it? I am getting confused a bit because there are so many people doing it different ways. I know with higher temperatures at the begginning you have a chance of shocking the parts but if you dont have the higher temperatures at the