Electronics Forum | Wed Mar 19 08:38:13 EDT 2014 | davef
I can't picture much of what you're saying, not for nothing, I'm just not connecting. During assembly, solder mask can affected by heat and chemicals. Typically this would be during: * Soldering * Cleaning I will tell you this: Not to defend assem
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Tue Mar 25 13:55:05 EDT 2014 | horchak
Ok lets put it this way. If the PCB house used a high quality mask and properly applied it to a properly cleaned surface and properly cured it, then as Dave stated above there are only two things that can destroy it. Excessive heat and overly aggress
Electronics Forum | Mon Apr 17 19:30:27 EDT 2000 | Boca
All of the above is good stuff. To add, I have seen this several times if the assembly is wavesoldered. Heat from the wave can partially reflow the top side SM solder joints and weaken them. To test, check joint strength before wave and then after
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Tue Mar 20 15:59:15 EDT 2007 | blnorman
We use preprinted labels and laser coding. For PCB we laser mark with CO2 (NdYAG for the aluminum heat spreaders). We either have an epoxy legend to burn out or we burn the solder mask to expose the copper ground plane underneath. Laser is a much