Electronics Forum | Tue Jun 29 16:09:44 EDT 1999 | Dave F
| Could somebody tell me what means Leaching, ie: "Leaching of terminal end face exposing the ceramic"? | Roberto: Leaching, according to the SMTnet Library of Terms: Leaching. Dissolution of a metal coating into liquid solder. Nickel barrier unde
Electronics Forum | Thu Aug 26 10:03:17 EDT 1999 | Sal
| | Could somebody tell me what means Leaching, ie: "Leaching of terminal end face exposing the ceramic"? | | | Roberto: Leaching, according to the SMTnet Library of Terms: | | Leaching. Dissolution of a metal coating into liquid solder. Nickel ba
Electronics Forum | Thu Jan 03 10:21:06 EST 2008 | fsw
Hi all! Heres wishing everyone a Happy & Prosperous 2008!! We are a small OEM/CM that use Ni tabs in our design/applications. We have a request to use Stainless steel to reduce/eliminate the Ni content. Can Stainless steel be soldered? If yes, is ou
Electronics Forum | Tue Jan 08 18:24:32 EST 2008 | jmelson
If your wedding ring ever gets hot enough to melt solder, I sure hope your finger isn't in it at the time! On the original question, most stainless alloys have quite a bit of Nickel in them, so going to stainless will not ELIMINATE nickel, although
Electronics Forum | Thu Jan 03 14:01:24 EST 2008 | fsw
Davef, thnx for your reply. Sorry, forgot to clarify "our normal soldering process". We use standard Sn/Pb & SAC305 for our non RoHS & RoHS requirements. We only have a "No Clean" process, no aqueous flux is used. Hence our flux will be mild. As susp
Electronics Forum | Fri May 24 19:18:03 EDT 2013 | hegemon
The formula is a great help, where was it 20 years ago? LOL After running a few thousand different products over the years, you start to get a feel for what is going to be trouble with regards to falling off the bottomside during the secondary refl
Electronics Forum | Wed Jun 30 11:09:24 EDT 1999 | John Thorup
| | | Could somebody tell me what means Leaching, ie: "Leaching of terminal end face exposing the ceramic"? | | | | | Roberto: Leaching, according to the SMTnet Library of Terms: | | | | Leaching. Dissolution of a metal coating into liquid solder.
Electronics Forum | Fri Aug 22 00:25:20 EDT 2003 | mantis
Kenny, Out of curisoty why do you need to paste the vias.Is it due to contact reliability at test.Can these vias not be soldered during wave process (if any).Can the Style of probe used in the ICT test fixture not be changed to accomodate these unsol
Electronics Forum | Fri Aug 22 09:41:49 EDT 2003 | davef
Mantis: Kenny reflows paste on [wave solders] all via, not just the test via, to plug the via and provide for a pressure seal between the board and the test fixture. Beyond that, since solder is softer than copper [and fills the hole better], solde
Electronics Forum | Tue Aug 26 21:12:24 EDT 2003 | iman
depends if your water wash process is manual or automation? important is the water residue inside the via holes is adequately blown out. As long as the water-flux residue is out, testing down the line should not be a issue, at least from theory and o
.gif)