Electronics Forum | Wed Jan 11 15:01:28 EST 2006 | jsloot
I have a samsung CP40 that is taking an average of 2.5 minutes to load a step program. My CP50 takes about 30 seconds. Both machines are configured the same in regards to the computers, both the operating system and internal CPU for machine functions
Electronics Forum | Sat Jan 21 16:36:19 EST 2006 | gipos
Hi James, You can use the same flux for micro BGAs.The 529D we used for rework of high freq. CSPs and even w/out cleaning it still worked on 2.5GHz.We have not washed the flux for 6 months and the RF features of the circuits remain the same. No chan
Electronics Forum | Wed Jan 18 01:47:36 EST 2006 | pavel_murtishev
Good morning Manyhats, I have 2 years working experience with automatic DEK screen printers. DEK products are really very good and are able to produce repeatable high quality print. For example I never saw problems with paste deposition for finepitc
Electronics Forum | Mon Jan 16 09:08:33 EST 2006 | DannyJ
Has anybody tried this stuff? I was asked about it this morning and it sounds plausible from their website, minus "The small volume of spent material can then be inexpensively shipped back to P. Kay Metal for recycling" part. Website: http://www.p
Electronics Forum | Mon Jan 16 11:00:33 EST 2006 | frankp
Danny, I'm hoping to hear more about this, too. I've seen it mentioned in a couple of other posts, but so far Sara G. (Foresite Inc.) is the only regular SMTNet poster that's actually seen this stuff. Really curious about residues, and what kind of f
Electronics Forum | Wed Mar 15 16:53:53 EST 2006 | Wave Master Larry
WELL I heard rumblings from the engineering dept that they wanna try this stuff here at my place of emplyment. Im not so sure about this.I've always herd that dross is part of the solder joint and part of wavesoldering.As I said before Ive done this
Electronics Forum | Mon Feb 19 14:28:35 EST 2007 | John
To: Wave Master Larry, You are correct in one respect. There is always dross on the wave, but it is a result of oxidation of the tin and lead. It IN NO WAY POSITIVELY EFFECTS the solder process, in fact, dross trapped in the solder joint is a detri
Electronics Forum | Wed Jan 18 14:53:38 EST 2006 | Mike gipos
Hi all, Anybody can help us to find out which of these reflow owens is possible to convert to Pb Free: 1.Panasert REF-A 2.Universal Full Spectrum IR Reflow 150 3.Hollis Surf FCR310 4.Panasonic 2632 Which one is the best and which one is the nea
Electronics Forum | Fri Jan 20 12:23:08 EST 2006 | stepheniii
Get a FAST computer. Especially if you are programming for the MSF. I didn't like the old panapro and havn't used the new one much. But from what I did see, it's much improved even if it takes a long time to optimize programs. Put it on the fastes
Electronics Forum | Wed Jan 25 13:38:58 EST 2006 | mrduckmann2000
I have used Winslow preforms several times.....sometimes with great results and others with not so good. It just depends on the BGA. I have a custom ASIC that will not re-ball, Winslow has even had trouble re-balling them. I would suggest using an