Electronics Forum | Sat Oct 02 13:55:01 EDT 2010 | wingding
I have recently started working on FUJI IP2s and CP3s, and I need information on the MCS2 system. Anything on keyboard shortcuts or possibly where I can find any manuals on MCS2 would be helpful. And no, I don’t work in a museum.
Electronics Forum | Tue Nov 02 15:57:20 EDT 2010 | g2garyg2
Anyone have any experience with them? Looking > for a 1 or .5 meter conveyor and possibly a > loader. Good prices for new equip, wondering if > there is a reason why? PROMATION has the best price on new 1M and 600 mm conveyors. They are often
Electronics Forum | Mon Oct 04 15:01:18 EDT 2010 | lfaustini
Hello, I am the owner of a Zevatech FS-710 that I now want to put into production. I bough the unit at auction, and it had no documentation whatsoever. If anyone out there can e-mail me any .pdf's or anything for me to even begin to get familiar w
Electronics Forum | Mon Oct 04 18:48:43 EDT 2010 | rsthompson
I am trying to assess current industry thinking on the question of whether or not lead-free BGAs (SAC or other) can or should be soldered in a tin/lead process. It seems there are differing opinions on this and I'm wondering what some of you are doin
Electronics Forum | Tue Oct 05 14:34:40 EDT 2010 | 18424
I am trying to assess current industry thinking > on the question of whether or not lead-free BGAs > (SAC or other) can or should be soldered in a > tin/lead process. It seems there are differing > opinions on this and I'm wondering what some of
Electronics Forum | Tue Oct 05 15:21:48 EDT 2010 | mikesewell
Nothing wrong with using RoHS BGAs except that the spheres won't melt/collapse at normal leaded reflow temps. Reliability will questionable. Some people use a hybrid profile with a slightly higher temp (~230C)and a slightly longer TAL (60 -90 sec).
Electronics Forum | Wed Oct 06 17:50:00 EDT 2010 | jamyboy
IBM Intel motorola did exhaustive studies on this and found that the best thing to do is (as others pointed out) the PBfree BGA reaches 217 minimum and the time above 217 must be extended to allow mixing of the 2 alloys. See attached a little diddy
Electronics Forum | Tue Oct 05 16:53:31 EDT 2010 | loyrickie
Never seen, or worked on one of these machines. After turning the unit on and hitting f5 to return to origination, I receive error message "37- Head LOWER POS. SENSOR OFF!". I also have no service manual, just replacement parts catalog and operatio
Electronics Forum | Tue Oct 05 18:05:56 EDT 2010 | jry74
I have seen an increase in components with contaminated leads, mostly SMT parts. They give us solder wetting problems and insufficient solder joints. Our practice is to not use them and return them to the manufacturer. Are these parts solderable?
Electronics Forum | Tue Oct 05 18:06:21 EDT 2010 | jry74
I have seen an increase in components with contaminated leads, mostly SMT parts. They give us solder wetting problems and insufficient solder joints. Our practice is to not use them and return them to the manufacturer. Are these parts solderable?
.gif)