What are the added capabilites going from 7w to 20w, 355nm YAG laser I wanted to know what the added capabilities we now have are going from a 7w to 20w, 355nm YAG laser. Currently we support the following materials: http://www.bestlaser.net/mater
Electronics Forum | Mon Dec 14 10:51:02 EST 2015 | dyoungquist
We have a two Heller ovens, 1707EXL (2006) and 1707MK III (2014). We use them for lead and lead-free reflow soldering including all the tricky components such as BGAs. You may want to go with 8 or 9 zones if you are running high volume but a 7 zone
Electronics Forum | Wed Apr 13 10:05:58 EDT 2016 | donnie15
I am working on soldering an Large LGA module to a PCB and am having some issues with opens due to variation in the board flatness. I have tried adding more paste but get shorts and excess flux as I get above a 7 mil stencil. I have tried adding sol
Electronics Forum | Thu Apr 21 20:09:18 EDT 2016 | adamjs
I have tried adding more paste but get shorts and excess flux as I get above a 7 mil stencil. You do need the thicker stencil. To prevent the shorts, you need to have your pick-and-place machine probe the exact height of the board (at multiple loca
Electronics Forum | Tue Sep 14 18:19:53 EDT 1999 | Mark Deren
| | Is it possible to place 0402 components with a Fuji CP2? How about a CP4? What are the suggestions for 0402 machine placement? | | | | Any help would be appreciated. According to the latest Fuji America S.M.T. Report I have, 0402 (1005) compo
Electronics Forum | Thu Jun 14 23:21:30 EDT 2001 | oem boy
I am working on 0201 development for my company in the UK, and I am planning a rather extensive DOE for my reflow oven profile. I am planning on studying various ramp rates, soak times, times above liquidus, peak temps, etc... My biggest concern
Electronics Forum | Wed Apr 21 12:03:59 EDT 1999 | Michael N.
I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is about
Electronics Forum | Fri Aug 21 17:16:11 EDT 1998 | Wayne Bracy
| | Steve: | | Take a look at the attached url. As with all testing systems, tooling / fixturing is costly. But, not as bad as a bunch of "Bed of Nails" test fixtures. | | Glad you had one of those great weekends, had to spend mine fishing,, again
Electronics Forum | Fri Jun 26 08:00:45 EDT 1998 | John Klimek
I have a used Hollis machine that might suit your needs. The only problem is that it is an oil blanketed machine. It is a 7" Hollis Nova 175. Right now it is collecting dust. | | | | | | | | | | Is anyone aware of any papers/publications dealing
Electronics Forum | Fri Oct 05 11:59:54 EDT 2001 | mparker
I am looking to learn of possible causes and solutions for the following problem. A potential customer is demanding that I use a saponifier in the aqueous wash, he has lab test results of former CM's products that leads him to believe it is necessar