Electronics Forum | Fri Nov 06 02:55:10 EST 2015 | arct1c
Hi, we are looking for 1 or 2 new postreflow AOI machines to replace our old ones and possibly 1 prereflow AOI(we never had pre reflow before). In our company we run low volumes and high volumes. I have been looking at Viscom, Mirtec mostly, Cyberop
Electronics Forum | Tue Nov 10 15:25:37 EST 2015 | 31258
Good morning RedChili, This is Marvin from Saki America. I came across your post and I noticed that you are interested on 3D-AOI and 2D-AOI machines. We can offer pre-reflow and post-reflow full 3D-AOI and 2D-AOI for you needs. IF you have any ques
Electronics Forum | Fri Nov 06 07:46:33 EST 2015 | clampron
Good Morning RedChilli, I have worked with Mirtec for quite a few years. I have looked at some of the other machines mentioned but have no practical experience with them. I started with the Mirtec MV-2 (long ago)due to the success of this platform,
Electronics Forum | Tue Jan 31 10:59:55 EST 2006 | carterhoward
Hi All, I�ve been doing some research on the issue of running lead-free solder paste and leaded solder paste through reflow at the same time. The point with this would be to process all standard leaded components with Lead paste while also processi
Electronics Forum | Wed Feb 08 18:19:53 EST 2006 | Mike
No we didnt. All our images where visual.
Electronics Forum | Wed Apr 25 14:55:01 EDT 2012 | swag
DMI International
Electronics Forum | Wed Feb 01 06:02:59 EST 2006 | joe
Hi, SAC BGA's in a SnPb reflow process can be achieved by ensuring the temp. on the BGA is at a peak min of 220�C and a time above 207-210�C for 60 - 90 Sec. Lower temperatures have shown incomplete mixing of alloys and some voiding.
Electronics Forum | Fri Feb 03 16:40:24 EST 2006 | Mike
At my last employer, we ran a number of tests to make a "Hybrid" profile work (same profile Joe lists) . It worked great for everything but BGAs. The problem (6 months ago) was using parts not rated for lead free reflow temps. As the market fills wit
Electronics Forum | Mon Apr 16 18:49:40 EDT 2012 | tris101
Hi guys, I'm looking for some tooling parts and I hope you can point me in the right direction. We design basic in house reflow Carriers to surport boards during reflow. I would like to add clamps to our designs but I can not locate any off the she
Electronics Forum | Tue Jan 31 12:37:33 EST 2006 | carterhoward
I guess my biggest concern would be what will happen to the inner metallic layer of the leaded solder during the higher temperatures.