Electronics Forum | Mon Dec 02 12:52:40 EST 2002 | slthomas
We're trying a selective soldering pallet for the first time with mixed reviews. Are solder balls a prevalent problem with this process? Most of them seem to correspond with pallet wall locations....is it too much turbulence from the rotary chip wav
Electronics Forum | Tue May 26 22:13:15 EDT 1998 | Pat Copeland
R&D is currently designing a board with smt components on both sides of the board. They are adding a 16 pin IC Gull wing. on the bottom side of the board. I have asked for only caps and resistors to be placed on the bottom side. Is there a recommende
Electronics Forum | Wed May 27 14:35:52 EDT 1998 | Justin Medernach
| | R&D is currently designing a board with smt components on both sides of the board. They are adding a 16 pin IC Gull wing. on the bottom side of the board. I have asked for only caps and resistors to be placed on the bottom side. Is there a recomm
Electronics Forum | Tue Feb 27 11:03:09 EST 2007 | Marcin
Hi All, Anybody knows what is the minimum clearance between through hole component and chip component? Problem description: On bottom side of my pcb are only 0603 chip components mounted on glue. One of the component is located very close to hole
Electronics Forum | Sun Apr 25 12:05:50 EDT 1999 | Chrys Shea
| | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free solderin
Electronics Forum | Mon Apr 26 09:18:27 EDT 1999 | C.K.
| | | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free so
Electronics Forum | Fri Feb 04 13:07:46 EST 2000 | Graham Naisbitt
Casimir This is not an easy subject. How did you process the test pieces? Was the flux used correctly at the required and recommended level? Did it see the wave properly? I am not an advocate of no-clean but we do have customers who coat over no-cl
Electronics Forum | Sun Jun 07 09:43:11 EDT 1998 | Bob Willis
There are some guidlines on design and through hole reflow on my web site to download. Also on pin in hole reflow the SMTA Office has a document on using the tecnology. | R&D is currently designing a board with smt components on both sides of the bo
Electronics Forum | Wed Jan 12 10:05:20 EST 2005 | Dreamsniper
we are using polyimide boards 6 inches x 7 inches, 2.5mm thick, 12 to 14 layers, for aerospace industries. I am using a long bake of 12 hours at 70'C prior to manufacturing or exposure to elevated reflow and wave soldering temperature. If schedule i
Electronics Forum | Thu Jul 12 16:14:20 EDT 2007 | realchunks
Hi Scott, Hard to tell what kind of problem you really have. I guess you need to describe your process first. What kind of process are you using. Wave solder, reflow solder, etc.. What kind of flux are you using to solder with? Vaccum? What ar