Electronics Forum | Thu Jan 27 11:23:45 EST 2005 | russ
Well first off I wouldn't evaluate paste for a wave process. I would use solder bar instead. Flux - top side fillets and no shorting on the solder side, does it clean well after processing if using water soluble flux. How wide is the process win
Electronics Forum | Thu Mar 12 06:37:48 EDT 2009 | gregoryyork
I agree you are too cold for the profile get it up to 230C and possibly allow it to dwell a little longer in preheat as opposed to pushing up the reflow zone only. Sn90/Pb10 melts at 220C so 2C hotter than your profile so you are reliant on it alloyi
Electronics Forum | Thu Feb 11 15:07:49 EST 2010 | hegemon
With regards to the rework, size and mass of the PCBs is important, in addition to the size of the components that are to be reworked. You might be in the game with $6K (APE Chipmaster Hot Air machine with Preheater or similar setup) if you have sma
Electronics Forum | Mon Apr 17 19:30:27 EDT 2000 | Boca
All of the above is good stuff. To add, I have seen this several times if the assembly is wavesoldered. Heat from the wave can partially reflow the top side SM solder joints and weaken them. To test, check joint strength before wave and then after
Electronics Forum | Thu Jan 24 13:23:53 EST 2002 | Shawn
Thank you all very much for the responses. The solder is eutectic and the problem, as far as I can tell, has been around before I was here, 2+ years. The flow machine is a treiber with 2 bottom preheaters and 1 top. The solder pot temp is 500F +/-4F
Electronics Forum | Mon Dec 02 12:52:40 EST 2002 | slthomas
We're trying a selective soldering pallet for the first time with mixed reviews. Are solder balls a prevalent problem with this process? Most of them seem to correspond with pallet wall locations....is it too much turbulence from the rotary chip wav
Electronics Forum | Tue Dec 03 18:31:45 EST 2002 | slthomas
At the price of Durapol we'd never get the OK to have them made. The Al fixtures are cheap and a quick turn local item. As dense as the pth parts are I also don't think there'd be any room for any holes which I really think is the answer as far a
Electronics Forum | Fri Jul 13 11:33:54 EDT 2007 | realchunks
Just starting and already responsible for product quality and machine adjustment? Wow, you poor bastard. Ok, I will assume this problem happens on the bottom side of the board with a thru-hole IC. The short occurs on the side that doesn't have the
Electronics Forum | Mon Apr 26 09:46:05 EDT 1999 | C.K.
Chrys: I have checked all the basic elements of Wave solder joint formation: fluxing, preheating, and lastly soldering. For checking the fluxer, i used a product from ECD that's very similar to what you desribed called the flux-o-meter. It did a
Electronics Forum | Tue Apr 13 18:11:00 EDT 1999 | Jimmy Strain
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185