Electronics Forum | Mon Dec 02 18:01:12 EST 2002 | GSW
Hi, Try to check if there is water absorbed in the flux or the humidity around the wave area. possibly plating on barrels that might be damaged?
Electronics Forum | Tue Dec 03 15:26:07 EST 2002 | GSW
This might be a trival mundane suggestion but try to use non conductive plate to hold components. Probably even made of the pallet material. I am sure your pallet fabricator will have tons of scrap and he can help you find one. T
Electronics Forum | Wed Dec 04 14:09:52 EST 2002 | Vince Whipple
By the way, what type of preheaters do you have? IR? Convection? If you have IR, there may be a way to cheat. Vince W
Electronics Forum | Thu Sep 20 12:20:45 EDT 2007 | jsloot
What kind and what brand of gloves are people using for handling hot wave solder pallets? My operators are going through a pair a week. I need something better. Thanks
Electronics Forum | Mon Dec 16 16:35:55 EST 2002 | Jim Ferris
Randy, Steve & all, Can you guys point me in the right direction when it come to using selective wave soldering...I am trying to get in-depth information on the Pro's & Con's of having our supplier use this process for our PWA's. (I can see there ar
Electronics Forum | Mon Dec 02 16:19:11 EST 2002 | slthomas
Unfortunately it's nc or we'd be worrying about this on the fly. Non-contact is defintely and issue....this is an 18"x9" board with 1500 bottom side SMT parts that are scattered among the through-hole and vice-versa. We're currently using 7 hold-
Electronics Forum | Tue Dec 17 13:42:04 EST 2002 | robf
There are a few emerging technologies that have been growing in popularity for the past few years. Pin through paste, press fit connectors and selective soldering machines seem to be displacing custom fixtures. Most of the mixed technology boards o
Electronics Forum | Mon Jan 07 13:18:28 EST 2002 | mregalia
I work for a microwave company. On our lower frequency boards (
Electronics Forum | Mon Jan 07 20:37:15 EST 2002 | davef
For soldered areas, we like to keep gold thickness substantially below the maximum you propose. Search the fine SMTnet Archives for our discussions on the topic of acceptable levels of gold with solder connections. Let�s fix this �no one seems be s
Electronics Forum | Thu Sep 20 20:07:24 EDT 2007 | davef
As sources for heat resistant gloves, try: * National Safety Apparel * Radnor