| Has there anyone bold enough to try this in their shops? My cubemate just got through telling me that at his last shop, they had bare copper boards (no HASL, no OSP, no nothing), with minimal solderability problems. I'd hate to have to clean what
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Tue Mar 20 15:55:59 EST 2001 | CAL
I only inhale flux with a high IPA content.(joke for those who don't know me) I have seen the inside of duct work for our wave soldering machine............NASTY! DAVE F. is right! Flux contains a lot of bad stuff- Chlorides, Bromides, Flourides,
Electronics Forum | Tue Mar 20 15:59:27 EST 2001 | CAL
I only inhale flux with a high IPA content.(joke for those who don't know me) I have seen the inside of duct work for our wave soldering machine............NASTY! DAVE F. is right! Flux contains a lot of bad stuff- Chlorides, Bromides, Fluorides,
Electronics Forum | Tue Nov 13 21:59:42 EST 2007 | davef
This processes has the potential to cause barrel cracking and pad lifting, because the heating is very hot [troop crank-up the volume on their iron when they see thick boards] for a relatively small area on one side of the board. What do we suggest
Electronics Forum | Tue Nov 24 19:07:12 EST 2009 | gregoryyork
I agree Patrick many people blame the assembly fluxes when it is some other hygroscopic chemistry left on the bare PCB such as surfactents from the HASL process these will do exactly what the guy reported in his post fail then cool down and pass ever
Electronics Forum | Wed Apr 06 15:32:11 EDT 2022 | proceng1
I spoke with a Tech at Superior Flux. He confirmed that Superior 515 will absoluteley turn yellow at room temp. Hydrobromic Acid in the flux, as it binds the hydrogen gases off and the bromine turns yellow. What is weird, is that Tin Bromide is y
Electronics Forum | Fri May 05 14:30:11 EDT 2000 | C.K.
I'd have to disagree with the Electrovert applications guy. I'd recommend SLOWING down the conveyor between .5 to 1 FPM - effectively, you're REDUCING contact length (because contact length = dwell time * conveyor speed), hence getting better peel-o
Electronics Forum | Tue Oct 22 14:57:18 EDT 2002 | Jim M.
I use a water soluble flux to solder an LCD into gold plated through holes of a .031 circuit card. Problem is the current water soluble flux (850-33) is not made anymore (the drop in replacement has a different formuala and does not work). The main i
Electronics Forum | Tue Apr 28 08:51:35 EDT 2009 | davef
This is a snip from an ealier post here on SMTnet. Generally, solder pastes are comprised of: 90% solder powder, 5% flux, 4% solvents, and 1% activators [by weight]. Where: * Solder powder, when reflowed, is a metal bonding agent that mechanically