Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri Sep 24 10:57:18 EDT 1999 | Earl Moon
| Hi Folks: | | We've been having bridging problems on our fine-pitch QFP's, despite thorough inspection of paste height, volume, and placement accuracies....profiles look good also. | | The bridging is happening after coming out of reflow...one la
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Tue Mar 21 20:25:30 EST 2000 | Dave F
John: What�s the matter? Free gold � good thing for you, bad thing for your supplier. :^) Pre-tinning of gold plated leads is important to: � Prevent gold embrittlement of the solder joint � Determine if the leads are solderable prior to assembly (
Electronics Forum | Wed Jul 02 12:42:58 EDT 2003 | slthomas
Not sure how else to describe this. We've received some boards (1/2" x 3.5" x .0325" board built on panels of 24) with numerous resistors showing separation of the solder from the metallization at the top of the joint. There are 26 0805's on the bo
Electronics Forum | Thu Jun 17 21:31:06 EDT 1999 | Dave F
| | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | for example: | | | | Solder Bridge | | 1.verify amount of flux been aplied. | | 2.verify turbulance on your solder w
Electronics Forum | Thu Jun 17 22:10:48 EDT 1999 | Earl Moon
| | | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | | | for example: | | | | | | Solder Bridge | | | 1.verify amount of flux been aplied. | | | 2.verify turbulance on
Electronics Forum | Tue Apr 28 08:51:35 EDT 2009 | davef
This is a snip from an ealier post here on SMTnet. Generally, solder pastes are comprised of: 90% solder powder, 5% flux, 4% solvents, and 1% activators [by weight]. Where: * Solder powder, when reflowed, is a metal bonding agent that mechanically