Electronics Forum | Fri Jun 22 11:09:01 EDT 2007 | realchunks
Sup G! Normally when spray fluxers get neglected, the spray pattern is the first thing affected. To actually 'see' this, we cut out a piece of cardboard the same size and length of the board. Run it over the fluxer and then turn itover and look at
Electronics Forum | Fri Oct 12 13:47:49 EDT 2007 | stepheniii
Does anyone here edit Wikipedia? I just checked and couldn't find the IPC link listed there. I still think if you ask what the OP asked then wiki is a good place to start. I did find this interesting link. http://www.ventureoutsource.com/contract-ma
Electronics Forum | Tue Apr 01 17:14:11 EDT 2008 | aj
Hi, We only have 2 lines , but I dont allow any of the Ops to set them up, I did once and winded up with 10 damaged nozzles and cracked caps on the boards ... If the problem is as big as you say it is , you should really spend some time setting it
Electronics Forum | Thu Sep 18 23:56:56 EDT 2008 | trynders
am having wetting issues with two Burr Brown Op amps. Both are SOICs with NiPdAu lead frame finishes. I have attached a photo that shows a black streak the length of the lead (before soldering). This appearance is consistent of all leads and is exist
Electronics Forum | Wed Jul 08 06:02:59 EDT 2009 | stepheniii
Advertisements are not always 100% accurate on technical issues. You don't want instand static discharge. A wrist strap with no resistor could cause that. Therefore put in a current limiting resistor to make the charge dissipate slowly. Does anyone
Electronics Forum | Mon Aug 27 08:58:24 EDT 2012 | rway
Reese, > > We would agree about the value of an > ICT system, in a general manufacturing > environment. However, a couple of notes > apply: > > 1. ICT isn't a catch-all, either, and > should be used to verify the process, not > validate it.
Electronics Forum | Mon Sep 23 12:59:12 EDT 2013 | pauldavis4
New pcba supplier sent us first article pcbas (SMT, Wave & hand solder operations) that failed our testing due to no-clean flux residues found under ICs and around passive capacitors. Second lot came in and had 100% pass yield, but we still see a cl
Electronics Forum | Fri Sep 27 15:37:05 EDT 2013 | tuxlab
We are thinking of getting a small pcb assembly setup for a small manufacturing co-op here in Los Angeles. Our experience consist of manual soldering of through hole and smt components. A quick search suggests that there are a few turn key opt
Electronics Forum | Thu Jan 09 00:10:59 EST 2014 | lingakarthik
Hi guys, can somebody explain me why and how immersion gold is better than hard gold platting or vice versa? We are not going to do any welding operation over the Gold platted area, rather we just move a sliding contact over the gold pl
Electronics Forum | Tue Jan 20 04:43:33 EST 2015 | gragal
I need to replace a device which is in a 6-pin package which looks like SOT 23-6 / SC-74 style. The markings are D102/ 214B (D102 above 214B). I have checked numerous references to no avail. I think that the device is a comparator or op-amp with V