Electronics Forum | Mon Jan 07 20:37:15 EST 2002 | davef
For soldered areas, we like to keep gold thickness substantially below the maximum you propose. Search the fine SMTnet Archives for our discussions on the topic of acceptable levels of gold with solder connections. Let�s fix this �no one seems be s
Electronics Forum | Wed Jun 26 17:51:55 EDT 2013 | ryansmta
Thank you for your response and interest to help me with my research work. I am actually in need of the Reel Holder. I am aware of a few services that can package the treated 0402 / 0201 components into a tape and reel. I have also spoken to MidAm
Electronics Forum | Mon Aug 05 09:16:39 EDT 2013 | valeriusx
Greetings. I'm having some difficulties in configuring 2 old SIPLACE Placement Machines - 80S-15 and 80F-3. They are already installed, there are no errors on machines computers, but I can't configure connection between these machines and the line c
Electronics Forum | Tue May 26 10:52:02 EDT 2020 | spoiltforchoice
No idea, could be a weird translation error, but its certainly something I have seen . For an FLX they just ask for this "5-6 bar, clean, dry, oil free, filtered 2 µm, connection diameter 8 mm", 40litre/min Personally I would go with a mo
Electronics Forum | Thu Jul 06 13:29:42 EDT 2006 | Chunks
Unfortunately it's not what you know, but who you know. Sounds like it in your case. Tread lightly as this guy may become your boss. It happened to me. New guy comes in, couldn't tell the "red stuff" from the "gray stuff" (adhesive / paste in cas
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Sat Feb 05 09:08:18 EST 2000 | Dave F
Casimir: Let me expand on something that I said in my response to your thread on ionic testing. Generally, no-clean people don�t use ROSE testing as part of their process control, because the ROSE test is essentially washing your board in DI/IPA �
Electronics Forum | Tue Jun 16 15:01:58 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Tue Jun 16 15:00:12 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil