Electronics Forum | Wed Feb 09 22:08:45 EST 2000 | Dave F
Russ: You've got stop soft-peddling this stuff. This doesn't sound like "poor solderability." It sounds like "no solderability." It also sounds like you�re dead meat. Three places to call: 1 Board supplier to get their suggestions on unsolderab
Electronics Forum | Mon Feb 11 21:54:14 EST 2002 | davef
LONG TERM Your plans to buy a vaccuum bag resealer and a batch drying oven sound good as you say, but you�re correct. They will not help with this current situation. SHORT TERM If your connections are clean, free of pits and holes with a smooth,
Electronics Forum | Wed Sep 10 09:32:56 EDT 2003 | swagner
Dave F, so what kind of problems would I see if this turned into a problem?
Electronics Forum | Thu Sep 11 09:22:27 EDT 2003 | swagner
Is there any conceivable way this could cause a tombstoned device?
Electronics Forum | Wed Aug 27 15:05:16 EDT 2008 | omid_juve
nothing relates to ROHS components and tin lead process?
Electronics Forum | Thu Aug 28 14:22:24 EDT 2008 | vladig
That is why you need to do analysis of the failed components first!!! Regards, Vlad www.sentec.ca
Electronics Forum | Thu Aug 28 14:42:30 EDT 2008 | grics
Vlad, Where might one do this analysis???
Electronics Forum | Fri Aug 29 14:51:19 EDT 2008 | wavemasterlarry
Vlad; you should pay for advertising like everyone else on this site.
Electronics Forum | Tue Sep 09 14:58:04 EDT 2008 | vladig
Hey Greg, Do you still want to see the answer? :-) Vlad
Electronics Forum | Wed Sep 10 04:23:42 EDT 2008 | gregoryyork
Wheres the Gold layer on the non wetted part of the pad