Electronics Forum | Wed Jul 29 12:14:30 EDT 2015 | davef
There is no current standard for the amount of flux that should be applied to a board. Current standards focus on what the result of a process should be, not how the process should be performed. So, the standard tells you that you need a procedure de
Electronics Forum | Tue Dec 28 21:51:04 EST 2004 | KEN
When using a foam fluxer: 1. Bubble size is important. What stones are you using? Ever clean them? Too large a bubble will NOT help your situation. (I forget bubble size range....check with your fluxer mfgr.) 2. Thinner will help in capilary m
Electronics Forum | Mon Feb 16 16:52:51 EST 2015 | joe98375
Hello, We are buying a Vitronics-Soltec wave solder machine with a spray fluxer to replace our old Econopak that has a foam fluxer. Currently we thin our flux (Kester 951) in the foam fluxer per Kester PS-20 and PS-22 test kits with kester 110 thinn
Electronics Forum | Wed Feb 01 10:13:39 EST 2006 | kmorris
I haven't seen a hydrometer used in years. Are > you still foam fluxing? There used to be > automatic units available, but with the advent of > the spray fluxer, they may have dried up. If you > are still foam fluxing with alcohol thinner, >
Electronics Forum | Mon Dec 18 11:04:43 EST 2006 | Steve
Are you making sure that the all the alcohol in the stone is pretty much gone before you put it in the tank? If the stone is dripping with alcohol when you put it in the tank, you could be affecting the specific gravity of the flux so much that it ca
Electronics Forum | Mon Sep 20 12:35:01 EDT 2004 | Rob
Hi Adam, We had a reverse of the previous - if we didn't have our smartwave running at at least 750 RPM behind the main wave, the pressure dropped & gave us inconsistant soldering. Otherwise... 1) are the components tarnished at all, or stored in
Electronics Forum | Wed Apr 04 14:29:16 EDT 2007 | rgduval
Anyone have experience wave soldering rigid flex assemblies? I've just picked up a new job from a customer; it's a rebuild for the company, but new to me. The customer had previously taken their business elsewhere due to delamination problems with
Electronics Forum | Wed Dec 04 09:24:52 EST 2002 | jseagle
I have found that preheating the solder pallets prior to use helps cut down on the solder balling. Also, we do not cool the pallets between passes and we use a spray fluxer because a hot pallet will knock down the head on a foam fluxer. We use WS f
Electronics Forum | Mon May 03 17:23:24 EDT 1999 | Kelly Morris
I am about to embark on an effort to evaluate 3 different solder material suppliers and their recommended materials for our assembly process, in an effort to find the best supplier/material. We do mixed technology, with NOCLEAN chemistry so I will b
Electronics Forum | Fri Dec 08 23:02:24 EST 2000 | LeeKibler
Beware the foam fluxer. I had a problem with cracked caps that just about drove me off the deep end. I discovered that my foam fluxer air knife was not turned on resulting in excessive flux. The excessive flux (VOC free) was not properly dried off