Electronics Forum | Mon Sep 25 08:15:53 EDT 2006 | egrice1@wi.rr.com
Most companies are double sided paste and reflow, then selective soldering the thru-hole. This will give you the best results and with much more consistency than with Wave Soldering.
Electronics Forum | Tue Aug 28 07:36:25 EDT 2007 | davef
If the copper on your PTH is not one thou, you will get blowholes. With the cost of copper going through the ceiling, you will get less than one thou of copper plating from substandard suppliers. Consider baking your boards prior to wave soldering
Electronics Forum | Thu May 15 13:42:12 EDT 2008 | sliebl
Typing "Optimizer Wave Solder" in Google brought back this: http://www.techinfocorp.com/wso/howandwhy.htm I have no relationship with this company.
Electronics Forum | Sat Aug 23 12:47:54 EDT 2008 | bruna
Hi! Does any one can give the reason of the black dust into de wave solder machine. We can found no reason for that, but the machine get dirty to fast despite the maintenance. Thanks for your time Bruna Neto
Electronics Forum | Tue Aug 08 12:49:33 EDT 2023 | serge_pirog
I ask for advice on starting wave soldering machine. The soldering machine is not new. Are there guidelines for properly loading solder into a bath and more. I also ask you to recommend an alloy. What do you think about Alpha Sn Plus 07 or SN100C(Sn
Electronics Forum | Thu Jan 15 03:20:59 EST 2009 | sachu_70
Hi Andrzej, I guess you mean peelable solder resist. Good idea to try during R&D, but certainly not a solution on production floor. Also, few constraints to be considered such as presence of entrapped air between component and solder resist, the natu
Electronics Forum | Mon Sep 03 06:17:19 EDT 2007 | mun4o
hi, This is moisture problem, I think.I have similar problem.You must try to bake PCBs.I bake our PCBs in solder wave mashine , under solder pot.There T is about 80*C - after 6-8h the PCB is dry regards
Electronics Forum | Thu May 15 22:02:29 EDT 2008 | davef
The question you should ask is: What's the difference between an Optimizer and a WaveRider?
Electronics Forum | Fri Dec 01 07:46:41 EST 2006 | davef
Bridging Causes: * Insufficient flux * Excessive pre-heat * High conveyor speed * Solder contamination
Electronics Forum | Fri Feb 14 22:03:40 EST 2003 | caldon
Air liquide has some great articles on this www.airliquide.com Cal