Electronics Forum | Mon Dec 18 23:24:50 EST 2006 | grantp
Hi, Yes, I would hate to resort to cleaning, but the product must be clean. We have been using palettes to keep most of the flux off the PCB, but there is still residue around the connectors. Does anyone suggest a good no clean flux to use with le
Electronics Forum | Wed May 07 15:36:04 EDT 2008 | llaerum
The 483 is what we use on all boards except on one where the 353 improved wetting on resistor packs. It worked much better since the parts are LF and this is the same flux AIM uses in their LF solder. Yes, it was recommended by AIM when we discussed
Electronics Forum | Thu Oct 02 17:00:44 EDT 2008 | davef
Is that accurate? If so, what are your aspect & area ratios? [Similar to the JerryS comment above.] * You say, � � and the average height is very high: nearly 200 pct.� => Our troop can make paste that height too. They snap the stencil-off a fast as
Electronics Forum | Thu Mar 10 10:06:08 EST 2005 | steve
OK all you Gurus here's one for ya. Customer is tinning wires with standard eutectic solder in a solder pot. There is a blue tint to the solder in the pot. After tinning with OA flux, which I will change to NC shortly, he has clear teflon insulation
Electronics Forum | Fri Mar 14 11:25:02 EDT 2008 | hegemon
ol' hege has got to agree with Chunks and Dave. Seems every time there is a problem, the finger is first pointed at the process. For my $.02 it doesn't matter if your process is 100% bulletproof, procurement will screw it up by finding a vendor that
Electronics Forum | Mon Feb 24 16:30:07 EST 2020 | stephendo
You might be able to get a step up transformer although I would not recommend that unless it is a good solution for you. What is the input voltage to your facility? It is probably 600V (or something close). If so then you could get a step down transf
Electronics Forum | Tue Feb 25 17:03:33 EST 2020 | kylehunter
LOL! Good to know! Yeah, we have 3Ph with a high leg, so technically at 240V, so we should be fine. Since nobody has really mentioned a real preference with the ovens, is it kinda like what I thought at first? That an 8 zone oven is an 8 zone oven.
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Wed Aug 21 17:44:32 EDT 2002 | davef
Splitting hairs, I expect SIR of all solderability protection, including OSP, to decrease after reflow. What�s more, I expect the SIR of all solderability protection to pretty much decrease over time. The �comb pattern� test specimens meet requirem
Electronics Forum | Mon Feb 19 11:36:39 EST 2001 | billschreiber
Hello Mark, I wish it were that simple so I could direct you to a particular manufacturer and stencil cleaner model. Unfortunately, there are several issues complicating the process of cleaning all these applications in one machine. First and fore