Electronics Forum | Tue Aug 27 13:30:32 EDT 2019 | surfacemountprocess
Hope this helps - http://www.surfacemountprocess.com/surface-mount-troubleshooting-guide.html
Electronics Forum | Tue Aug 27 13:55:47 EDT 2019 | vchauhan
Excellent. There are lots of information. Thank you.
Electronics Forum | Tue Sep 28 12:23:07 EDT 2021 | aex
reflow profiles are actually 20F above set points
Electronics Forum | Wed Mar 23 19:36:21 EDT 2022 | tey422
ECD SuperMole
Electronics Forum | Fri Mar 25 13:33:50 EDT 2022 | kojotssss
https://www.solderstar.com/en/
Electronics Forum | Thu Jul 13 04:56:29 EDT 2000 | dutkell
John, I totally agree with you on all your above comments. You obviously have a real grasp of your subject, and are very knowledgeable. My colleague and I would like to take this opportunity to request information on personnel ' training' aspects re
Electronics Forum | Sun Apr 13 19:50:20 EDT 2003 | yukim
Hi, We are placing (+) & (-) terminals in SMT. We have just changed the plating of them: from Nickel to Tin (Sn). During the trial, we used the same reflow profile as before changing, and the solder seems different: a bit cold, with some solder paste
Electronics Forum | Tue Jul 06 00:23:11 EDT 2010 | cksam
I am doing the case study of the component chip 0201 tombstoning problem. The significant causes was the reflow profiling preheat slope or ramp up rate. I really can't differential between preheat slope and ramp up rate. Could anyone here show me the
Electronics Forum | Sat Jul 22 11:38:18 EDT 2017 | vchauhan
We normally do reflow profile on non-populated solder sample board. We do use some critical component like BGA and put thermal couple underneath. I need your expertise. How much will it drop in peak temperature when we will be running populated board
Electronics Forum | Mon Feb 18 15:44:49 EST 2008 | ck_the_flip
Yup! All the major players out there - KIC, Datapaq, and ECD - are all capable of profiling both reflow and wave solder. check them out. www.kicthermal.com www.ecd.com www.datapaq.com