Electronics Forum | Wed Nov 06 05:13:01 EST 2002 | Dreamsniper
Crystalline flux if it is really clear should not be a problem. We were using Amtech paste before and we have the same results. Sometimes we mistakenly see it as a dry joint because of the reflections from the lighting of our Metcal inspection system
Electronics Forum | Wed Mar 05 03:43:58 EST 2003 | testing
Hi, Mike Thanks for the reply With your oracle system were you able to perfom SPC analysis? and if possible do you have any Material that may be helpful for me to get my system setup i.e. whether through Excel, Access, Oracle etc. + What are your
Electronics Forum | Wed Sep 10 12:56:09 EDT 2003 | davef
Intermetallic compounds [IMC]: * Form during the alloying process of some metals. In soldering these are Sn, Ni, Ag, Cu, Au. * Do not accept solder. * Increase in depth in logarithmic proportion to both time and temperature. [So during the solder
Electronics Forum | Tue Jun 29 14:42:55 EDT 2004 | davef
You're correct, for every dumpster full of paper written about solder, there's a sentance written about fluxes. There's dribs and drabs about fluxes in most of the soldering books [ie, Manko, Klein-Wassink, Judd, Strauss, etc] and most of that is ve
Electronics Forum | Tue Jan 04 15:28:22 EST 2005 | davef
Look here: * Circuit Board Repair and Rework Guide [ http://www.circuittechctr.com/guides/guides.shtml ] * 7711/21A - Rework and Repair Guide [ http://webvision.ipc.org/scripts/mgrqispi.dll?APPNAME=IPCWEB&PRGNAME=TOCFRAME&ARGUMENTS=-N,-N,-A,-A,-N50 ]
Electronics Forum | Sat Feb 05 14:51:49 EST 2005 | etienne
One important thing to look at, when buying an AOI is the False Calls Rate, along with tact time of machine to inspect the PCB. Obviously, many machines can do the the work....but it's also true that each machine differ from the way it do the work. S
Electronics Forum | Wed Feb 09 12:28:58 EST 2005 | Valerie
We have been pretty successful with screen printing glue, however the smallest component we now glue is a 0805. We had many problems using our Gemini II to put down glue dots for a 0603, so we altered the pads to do double-side reflow. As our own int
Electronics Forum | Wed Feb 09 21:19:03 EST 2005 | Mrduckmann2000
Russ, We can not use a wave pallet, already went that route. We have parts next to the thru-hole pins and between thru-hole pins. I am going to try an experiment in the next day or so with solder mask. I plan to solder SMT parts on the back of se
Electronics Forum | Fri Aug 26 09:57:21 EDT 2005 | russ
The Immersion gold is not a problem with BGAs specifically but "black pad" which can be present anywhere. The unfortunate thing with BGAs is you cannot see it. Personally I hate white tin. It is okay for single sided boards running no-clean, but c
Electronics Forum | Tue Sep 29 11:49:02 EDT 2015 | spoiltforchoice
Typically - hand soldering as you are currently doing. Should your volume justify it you can invest in a selective soldering solution, these might take the form of a robotic arm that essentially replicates manual soldering or a solder jet similar to