Electronics Forum | Thu Mar 30 13:09:08 EST 2006 | bvdb
The cover tape that seals the parts into the reels on our feeders always uncovers a few parts (up to ten 0805 parts) before the part can be picked. So removing a partial reel always results in the loss of a few parts. Putting a partial reel back on
Electronics Forum | Wed Apr 19 06:56:54 EDT 2006 | QTEK Manufacturing Ltd. www.qtek.com
QTEK Manufacturing Ltd. provide a solution to the above problem, QTEK Cover Tape Extender adds an extra 380mm to cover the tape of component reels. It saves components being wasted or discard when strating a new tape through a feeder, and enables the
Electronics Forum | Mon Apr 03 11:48:31 EDT 2006 | stepheniii
How big are the parts? I've only seen a few parts that ever fell off. Double sided reflow is probably the most common these days The surface tension is powerful. I think the lower limit of temperature is what you would have to worry about with epox
Electronics Forum | Thu Apr 06 04:38:21 EDT 2006 | dougs
Hi, We have just purchased a new rework station, i'm looking for tips to get the best quality rework possible. Currently when we are replacing a SMT component we take off the old one clean the pads with solder braid then IPA, re-tin the pads the
Electronics Forum | Thu Apr 06 16:42:44 EDT 2006 | russ
this is all good jay but would WML have to say about this paste? I'm gonna wait for his response before I do anything! I am bringing in some samples of this soon to try for myself. I have a part that the manufacturer says to run with a paste with n
Electronics Forum | Thu Apr 06 17:02:48 EDT 2006 | jbrower
I'm just dying to hear. I think this past will be a contender for us, I'd use it but I allready commited to using the Kester EM907. Maybe after the first of the year I'll look at switching to this paste. Ive never heard of a problem like that, but
Electronics Forum | Fri Apr 14 07:59:42 EDT 2006 | amol_kane
Hi russ, I am in the process of developing a "hybrid" reflow profile to solder a board that has LF BGAs and leaded solder. Have you encountered a similar situation before? if so what was the "safe" top side temp for the leaded components that was set
Electronics Forum | Fri Apr 21 07:44:04 EDT 2006 | amol_kane
yes! i though this thread looked familiar! looks like it has been repeated....even the response from muse is very very familiar...that, or i am have a serious attack of deja vu! thanks for the requote though.......by doing some research I decided to
Electronics Forum | Fri Apr 07 12:35:14 EDT 2006 | Chunks
Hi Chim Chim, Hows Spritle these days? You guys still living in the trunk of the Mach 5? Tell Trixie, Mom , Pops, Sparky, Racer X ans Speed I said "Hi". BTW, The Shooting Star (#9) was way faster than your brother Speeds. All be it that it took
Electronics Forum | Mon Apr 17 14:08:51 EDT 2006 | russ
So far the only issue I have been able to determine with this product is Pkaymetals the company. Seems impossible to get samples or local representation. Was told first that they would not let me have it until they had local representation so equip