Please help to answer me the followings questions: 1. The optimum temperature for IC reapir (TSOP & BGA), since many IC found defective after reapir by hot air gun 2. How many time does a IC(TSOP & BGA) can pass throught the IR Reflow without defecti
Electronics Forum | Mon Oct 08 09:48:22 EDT 2007 | slthomas
I used to just follow up profile development with a single pass with a MOLE, one thermocouple in air. I'd keep that profile as a baseline, and have the operators run the MOLE through prior to production and compare the results to the baseline. I foun
Electronics Forum | Wed Dec 05 10:58:59 EST 2007 | shrek
Mr. Long, me lad, I don't follow. You say stuff about RoHS and all the banned materials covered by RoHS, but what is your theory on how banned substances can get on a RoHS board if you are running both Pb and Pb-free on the same oven?
Electronics Forum | Tue Dec 18 22:20:54 EST 2007 | darby
Paul, For the Dek and following equipment - seperate all the "bad fid" pcbs and process them seperately. Drill a hole as accurately as you can through the bad fids making sure you leave some white area around them. Set up and run a seperate program u
Electronics Forum | Tue Dec 11 16:55:11 EST 2007 | dman97
Hi, I am using a 7 zone Conceptronics oven and Indium 3.1 lead free clean paste. Our profile is as follows, 130 140 150 180 200 240 260 with a belt speed of 36 inches per minute. I dont know if that will help you out though...
Electronics Forum | Thu Dec 20 16:32:54 EST 2007 | gsala
Over here in Eurolandia the following Allois are running like a piece of cake. http://www.krepro.no/tinn_pasta_fluss/NiGe-Stangtinn.pdf It is FUJI patent Formula, sold in Eurolandia by FELDER Germany Really a good help in the Lead Free Wave Solder
Electronics Forum | Fri Jan 25 18:22:03 EST 2008 | mobytahoe
We have evaluated (in-house) the following machines: Agilent SP50, CyberOptics SE300, Siemens OS. We have also evaluated the MVP machine and the Orbotech machine off-site. Best bang for your buck??? CyberOptics by far! Better Gage R&R, better standa
Electronics Forum | Wed Jan 09 13:03:22 EST 2008 | patrickbruneel
Matte solder mask greatly reduces the potential for solder balls, and since you altered the machine parameters with no improvement it might be flux related. Do you use a VOC free (water based) or alcohol based no-clean flux? Do you use machine settin
Electronics Forum | Mon Jan 14 12:35:28 EST 2008 | dphilbrick
Jay Go to the Services menu and then station configuration. Choose your F3 machine from the list. This will open the tool that allows you to configure what the machine has on it. Look to see if you have a box with the following: WPC-TR S_WPW_80F
Electronics Forum | Wed Jan 23 20:11:14 EST 2008 | davef
In previous threads, similar to this here on SMTnet, varies folk have made recommendations, as follows. Fixed position (mounted) [In-line] laser bar code scanners: * microscan 800-762-1149 info@microscan.com [Ken SMTnet] * symbol technologies symbol.