Electronics Forum | Wed Oct 02 18:18:58 EDT 2002 | davef
The steadfast rule of thumb is: In order to get reliable reflow, you need to be at or higher than [liquidus + 20�C] for about 5 to 10 seconds, rather than those old "60 seconds above 183�C" guideline. This provides for setting your peak based on the
Electronics Forum | Mon Dec 22 12:06:27 EST 2008 | evtimov
Hi, it seems like a glue problem to me. If you don't have enough glue on SOT23, you have no contact and the part is holded only by the paste, which results bad in the waver machine. So first I would check is the glue amount under the SOT. The second
Electronics Forum | Tue Jul 06 19:45:03 EDT 2004 | ANDREW
Based on the attchment it looks like both are low profile and cater for high IO point.What are the challenges in running this 2 type of component?Is there any additional process required other than normal SMT for these 2 packages,like underfill ?
Electronics Forum | Wed Jun 21 09:12:42 EDT 2017 | emeto
I would start with checking the flux amount and trace and the thermal profile(preheating is important) for this assembly. Then I would consider changing to another flux and run it again.
Electronics Forum | Thu May 20 03:45:22 EDT 2021 | jineshjpr
SAC305 Will be the best choice with minimum TAL, Maximum Soak Solder Profile. Surely your solder Joint strength also will be more reliable & This can pass any kind of reliable Tests.
Electronics Forum | Wed Feb 18 12:42:43 EST 2004 | babe
OK, if the sphere of the ball and the paste on the pad are both eutectic, 63/37 then the paste will reflow first causing a drop of the component, after which the spheres will reflow causing a double drop and a good intermettalic. You can see this by
Electronics Forum | Wed Sep 15 09:17:52 EDT 2010 | eniac
Hi all! Does any body know which company is real manufacturer of this reflow ovens? Manncorp is only distributor (and in USA), I can't buy it in USA and move to Eastern Europe :( I need to find who produce this ovens, can somebody help to me? Than
Electronics Forum | Wed Aug 12 03:43:01 EDT 1998 | Terry Keen
We are taking enquiries for sub-contract work that we hope to be doing by Christmas. One of the enquiries is to assemble chip capacitors and an SO14 onto ceramic. Does the printing process, paste used and reflow process remain the same, or are there
Electronics Forum | Mon Nov 21 16:34:03 EST 2011 | davef
Google: nitrogen reflow tombstone https://www.google.com/search?q=nitrogen+reflow+tombstone&ie=utf-8&oe=utf-8&aq=t&rls=org.mozilla:en-US:official&client=firefox-a
Electronics Forum | Tue Nov 02 05:00:28 EST 2004 | jysam
we are using solder paste WS609 and OM5100.Relow oven: forced convection type. For WS609 and OM5100, straight ramp up profile is suitable for low to medium thermal mass assemblies and preheating may be required for high thermal mass assemblies. How