Electronics Forum | Fri Aug 13 10:19:35 EDT 1999 | Boca
| | We are using a mixed technology process with mostly through-hole parts plus some SMT IC's on the component side and some passive SMT parts on the solder side. We do not have a proper wave soldering machine for doing solder side SMT (double wave
Electronics Forum | Fri Jun 25 12:01:49 EDT 1999 | Earl Moon
| | Dear John/Earl | | | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the Desired
Electronics Forum | Sat Jun 12 10:46:32 EDT 1999 | Dean
| Our company is experiencing cracked caps at our pick and place operations. The caps are being placed onto epoxy dots for subsequent wave solder operations. At present, be have set the pressure of the head at 2 in/lbs. This being down from manufac
Electronics Forum | Thu Mar 25 14:13:13 EST 1999 | Bob Willis
| | I am looking for clip art images of electronics assembly. Images like wave soldering, surface mount components, soldering irons... just general assembly graphics. Many sites have different individual images that they use I was just wondering if
Electronics Forum | Mon Jan 25 10:59:01 EST 1999 | Ng
| | It has been known that sufficient cooling after soldering is important in order to get a stronger joint during its solidification stage. And it has been so much emphasised with reflow oven. But, why many models of wave soldering machine do not co
Electronics Forum | Mon Sep 17 17:09:32 EDT 2001 | jschake
Flux: No-clean pastes tend to have a wider print process window in terms of print speed and pressure. More importantly, no-clean pastes are more tolerant to changes in temperature and humidity. They also exhibit longer stencil life than water-solub
Electronics Forum | Mon Nov 05 20:31:09 EST 2001 | davef
Most people do not intend to �solder� Type K thermocouples. They use solder to �attach� the thermocouple. Search the fine SMTnet Archives for a posting by Chrys Shea. 1 Common thermocouple types commonly used for thermal profiling are: * Type K �
Electronics Forum | Tue Feb 19 19:39:22 EST 2002 | davef
Wow!!! A cleb, coo!! I thought roadies were not only ugly, but BIG and ugly. Yes, it was a nice one, but I coped it from an Ozzie football club chat site. No pretense at being that astute. Yeh, it sounded like the licensed club was closed, but n
Electronics Forum | Thu Jan 20 17:14:39 EST 2005 | jbrower
Today, I have just finished evaluating Kester's EM907 (SAC305)lead free solder paste and found that for our applications it performs as expected. End result that I am encouraged with the results that we got. The equipment that I used: An SMT2020 to
Electronics Forum | Fri Jan 13 06:43:20 EST 2006 | cyber_wolf
How would you like to have this guy evaluate your reflow profile? It was in response to an auditor who require someone they had monitor temperature in both Fahrenheit and Celcius. What a geek Don't put him on the spot. That is not a good thing to