Electronics Forum | Tue Apr 11 10:30:46 EDT 2000 | Jeremy Smith
I am having a problem with some joints on a 100 pin pqfp and few different soics on one particular board. When viewed a 8x with a "Mantis" inspection scope the joints look as though they wetted to the ic leg but when probed the leg will pop loose.
Electronics Forum | Tue Apr 11 20:26:16 EDT 2000 | Dave F
Jeremy: Parts assembler make leads of either Alloy 42 (Invar, whatever) or copper. The solderability of these leads are protected with eutectic or non-eutectic tin/lead solder, palladium or some palladium alloy, or gold. Cuppla things to consider:
Electronics Forum | Thu Jun 07 05:11:42 EDT 2012 | cp38260
Hi, I have pcbs (Duroid/RT 5880) with raw copper, soldered in vapour-phase chamber at 230 degrees Celsius. During soldering, copper gets tarnished. Cleaning with Vigon A250 removes the tarnished layer. Indeed, in the VigonA250 techn. datasheet it is
Electronics Forum | Thu Apr 15 11:15:30 EDT 2004 | patrickbruneel
Pure (red) copper oxide is green, its not a residue its just oxidation. In your case water and heat will accelerate the oxidation process of unplated or unprotected pure copper. The best way to avoid this from happening is use a socket with tin or n
Electronics Forum | Thu Apr 15 08:23:47 EDT 2004 | prod
hi, Having put a copper socket trough a wave soldering machine, and then through a DI wash, the boards have been dried and after a few days a green residue has been noticed on the copper. any suggestions? not drying properly maybe? or could it be th
Electronics Forum | Fri Apr 16 11:03:35 EDT 2004 | davef
Your copper corrosion is not good. It indicates that you have not done a good job in cleaning. [We assume this is a medium green color, not unlike the color of the solder mask on your board, that is almost like a translucent lacquer; rather than th
Electronics Forum | Wed Apr 04 19:25:58 EDT 2007 | TB
Dear All, anyone has experienced with thin layer of immersion tin (about 5 microns) on copper pads in term of long term reliability for first or second reliability studies. Any input will be greatly appriciated.. Thanks.
Electronics Forum | Mon Dec 20 07:58:02 EST 1999 | pascal MATHIEU
hello guys ; we are using a fine pitch component(0.65mm) on a thick copper PCB (Cu = 90�m) ; in this case we notice that we are in the process'limits , because the different supplier of the PCB are not able to ensure a good stability of it's process
Electronics Forum | Sun Apr 08 14:15:24 EDT 2007 | davef
Look here: * http://ieeexplore.ieee.org/xpl/freeabs_all.jsp?arnumber=496035 * http://www.emeraldinsight.com/Insight/viewContentItem.do?contentType=Article&hdAction=lnkpdf&contentId=878290 * http://www.smta.org/knowledge/proceedings_abstract.cfm?PRO